Order Products : sales@su-jiao.com
Adiprene® LFP 2950A
| Category: | PUR-Capro/PPDI , Polyurethane (Polycaprolactone, PPDI) |
| Manufacturer: | Chemtura |
| Trademark: | Adiprene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | LbgByd_Adiprene-LFP-2950A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ADIPRENE LFP 2950A is a PPDI-terminated polycaprolactone prepolymer having very low free PPDI content (typical < 0.1%) for easier management of health and safety during handling. This prepolymer is similar to ADIPRENE PP 1096H in composition and performance. ADIPRENE LFP 2950A yields high performance 93-96 Shore A hardness elastomers when cured with VIBRACURE® A 250 or HQEE. The high performance features of ADIPRENE LFP 2950A are due to PPDI (p-phenylene diisocyanate), a special building block that imparts exceptional properties to cast polyurethane elastomers. The unique combination of properties exhibited by PPDI-based prepolymers is superior to those available from standard prepolymers based on TDI or MDI. Features of ADIPRENE LFP 2950A include:
|
| General Information | |
|---|---|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.15 | g/cm³ | ASTM D792 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A) | 94 to 96 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Compressive Strength | ASTM D695 | ||
| 5% Strain | 2.76 | MPa | |
| 10% Strain | 5.52 | MPa | |
| 15% Strain | 8.27 | MPa | |
| 20% Strain | 11.7 | MPa | |
| 25% Strain | 15.2 | MPa |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ASTM D412 | ||
| 100% Strain | 10.3 | MPa | |
| 300% Strain | 13.8 | MPa | |
| Tensile Strength | 44.8 | MPa | ASTM D412 |
| Tensile Elongation (Break) | 580 | % | ASTM D412 |
| Tear Strength (Split) | 25 | kN/m | ASTM D470 |
| Compression Set | ASTM D395B | ||
| 70°C, 22 hr | 45 | % | |
| 100°C, 22 hr | 60 | % | |
| Bayshore Resilience | 62 | % | ASTM D2632 |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Pot Life | 9.0 | min | |
| Demold Time | > 60 | min | |
| Post Cure Time (127°C) | 16 | hr |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Dynamic Properties | |||
| Storage Modulus : 30°C | 3.20E+8 | dynes/cm² | |
| Storage Modulus : 150°C | 2.10E+8 | dynes/cm² | |
| Tangent Delta : 30°C | 0.0150 | ||
| Tangent Delta : 150°C | 0.0130 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 1099 X 115081 E | RTP Company | PBT | RTP |
| Scolefin 33 G 12-0 | Ravago Group | PP Homopolymer | Scolefin |
| SynPlast™ TOTM-E | PolyOne Corporation | Tri (2-ethylhexyl) Trimellitate | SynPlast™ |
| Next Nylon 66 Prime Series PXR-01BK | Next Polymers Ltd. | Nylon 66 | Next Nylon 66 Prime Series |
| HIPOL™ J340 | Mitsui Chemicals, Inc. | PP Impact Copolymer | HIPOL™ |