ENGAGE™ 7467
| Category: | TPO (POE) , Polyolefin Elastomer |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | ENGAGE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | LavG6G_ENGAGE-7467.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ENGAGE™7467 Ethylene Butene Copolymer is a high-performance copolymer with excellent impact resistance and is used in TPO processing requiring stricter requirements. Main features:
Application field:
Comply with the following regulations:
|
| General Information | |
|---|---|
| Agency Ratings |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.862 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.2 | g/10 min | ASTM D1238 |
| Mooney Viscosity (ML 1+4, 121°C) | 19 | MU | ASTM D1646 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ASTM D2240 | ||
| Shore A, 1 second, molded | 52 | ASTM D2240 | |
| Shore D, 1 second, molded | 12 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus - 100% Secant 1(Compression Molded) | 1.40 | MPa | ASTM D638 |
| Tensile Strength 2(Break, Compression Molded) | 2.00 | MPa | ASTM D638 |
| Tensile Elongation 3(Break, Compression Molded) | 600 | % | ASTM D638 |
| Flexural Modulus | ASTM D790 | ||
| 1% secant : Molding | 4.10 | MPa | ASTM D790 |
| 2% secant : Molding | 4.00 | MPa | ASTM D790 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tear Strength 4 | 21.6 | kN/m | ASTM D624 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Transition Temperature | -58.0 | °C | Internal method |
| Melting Temperature (DSC) 5 | 34.0 | °C | Internal method |
| Peak Crystallization Temperature (DSC) | 13.0 | °C | Internal method |
| Additional Information |
|---|
| 对无滑石粉产品测量的属性。 |
| Note Message | |
|---|---|
| 1 . | 510 mm/min |
| 2 . | 510 mm/min |
| 3 . | 510 mm/min |
| 4 . | C mould |
| 5 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Rilsan® BESN P40 W5 TL | Arkema | Nylon 11 | Rilsan® |
| Enable™ 23-05 Series | ExxonMobil Chemical | mPE | Enable™ |
| ESTACARB PC 0820 V0 | Cossa Polimeri S.r.l. | PC | ESTACARB |
| ISPLEN® PP 045 G1E | REPSOL | PP Homopolymer | ISPLEN® |
| Lushan PF-300 | Guangzhou Lushan New Materials Co., Ltd | Polyolefin, Unspecified | Lushan |