LUVOCOM® 1105-7107 Datasheet,PEEK,Lehmann & Voss & Co.-SHANGHAI SUSHENG

Message
LUVOCOM®1105-7107 is a polyetheretherketone (PEEK) material, which contains a glass fiber reinforced material. This product is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific,. LUVOCOM®The main features of 1105-7107 are: flame retardant/rated flame Flame Retardant anti-warping Good dimensional stability chemical resistance Typical application areas include: textile/fiber engineering/industrial accessories Aerospace Automotive Industry medical/health care

General Information
Filler / Reinforcement	Glass fiber reinforced material
Features	Good dimensional stability Low warpage Good liquidity Good chemical resistance Hydrolysis stability Flame retardancy
Uses	Textile applications Engineering accessories Aerospace applications Application in Automobile Field Medical/nursing supplies
Appearance	Natural color

Physical	Nominal Value	Unit	Test Method
Density	1.41	g/cm³	ISO 1183
Melt Mass-Flow Rate (MFR) (380°C/10.0 kg)	58	g/10 min	ISO 1133
Molding Shrinkage	0.50 - 1.0	%	DIN 16901
Water Absorption (23°C, 24 hr)	< 0.10	%

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	7500	MPa	ISO 527-2
Tensile Stress (Break)	105	MPa	ISO 527-2
Tensile Strain (Yield)	2.0	%	ISO 527-2
Flexural Modulus	6500	MPa	ISO 178
Flexural Stress	145	MPa	ISO 178
Coefficient of Friction
Dynamic	0.30
Static	0.27
Flexural Strain at Flexural Strength	2.5	%	ISO 178

Thermal	Nominal Value	Unit	Test Method
Maximum operating temperature- Short Term	260	°C

Electrical	Nominal Value	Unit	Test Method
Insulation Resistance	> 1.0E+16	ohms	IEC 60167

Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength (23°C)	6.0	kJ/m²	ISO 179/1eA
Charpy Unnotched Impact Strength (23°C)	30	kJ/m²	ISO 179/1fU

Thermal	Nominal Value	Unit	Test Method
Continuous Use Temperature	250	°C	UL 746B
Vicat Softening Temperature	305	°C	ISO 306/A
CLTE - Flow	3.0E-5	cm/cm/°C	DIN 53752

Electrical	Nominal Value	Unit	Test Method
Surface Resistivity	> 1.0E+15	ohms	IEC 60093

Flammability	Nominal Value	Unit	Test Method
Flame Rating ¹	V-0		UL 94

Injection	Nominal Value	Unit
Drying Temperature
Hot air dryer, A	150	°C
Hot air dryer, B	120	°C
Drying Time
Hot air dryer, A	3.0 - 6.0	hr
Hot air dryer, B	6.0 - 8.0	hr
Suggested Max Moisture	0.050	%
Rear Temperature	360 - 370	°C
Middle Temperature	380 - 390	°C
Front Temperature	390 - 400	°C
Nozzle Temperature	360 - 380	°C
Processing (Melt) Temp	390	°C
Mold Temperature	170 - 190	°C

Injection instructions
General In general LUVOCOM® can be processed on conventional injection moulding machines while observing the usual technical guidelines. Any added fibrous materials or fillers may have an abrasive effect. In this case the cylinder and screw should be protected against wear as is usual in the processing of reinforced thermoplastic materials. Lengthy dwell times for the melts in the cylinder should be avoided. Lower the temperatures during interruptions! Predrying (optional) It is advisable to predry the granulate with a suitable dryer immediately before processing. The granulate may absorb moisture from the air. Delivery Form & Storage Unless indicated otherwise, the material is delivered as 3mm-long pellets in sealed bags on pallets. Preferably storage should be effected in dry and normally temperatured rooms Additional Information During processing, the moisture content should not exceed 0.05%. To avoid internal stresses, a medium to high injection rate should be used. An increase in tool temperature may be helpful. Post-crystallization may lead to warpage at elevated operating temperatures. This can be counteracted by suitable heat treatment. The processing notes provided merely represent a recommendation for general use. Due to the large variety of machines, geometries and volumes of parts, etc., it may be necessary to employ different settings according to the specific application. High-temperature polymers place increased demands on the tool steels employed. Please contact us for further information.

Injection instructions

General In general LUVOCOM® can be processed on conventional injection moulding machines while observing the usual technical guidelines. Any added fibrous materials or fillers may have an abrasive effect. In this case the cylinder and screw should be protected against wear as is usual in the processing of reinforced thermoplastic materials. Lengthy dwell times for the melts in the cylinder should be avoided. Lower the temperatures during interruptions! Predrying (optional) It is advisable to predry the granulate with a suitable dryer immediately before processing. The granulate may absorb moisture from the air. Delivery Form & Storage Unless indicated otherwise, the material is delivered as 3mm-long pellets in sealed bags on pallets. Preferably storage should be effected in dry and normally temperatured rooms Additional Information During processing, the moisture content should not exceed 0.05%. To avoid internal stresses, a medium to high injection rate should be used. An increase in tool temperature may be helpful. Post-crystallization may lead to warpage at elevated operating temperatures. This can be counteracted by suitable heat treatment. The processing notes provided merely represent a recommendation for general use. Due to the large variety of machines, geometries and volumes of parts, etc., it may be necessary to employ different settings according to the specific application. High-temperature polymers place increased demands on the tool steels employed. Please contact us for further information.

Note Message
1 .	Not recognized by UL.

Category:	PEEK , Polyetheretherketone
Manufacturer:	Lehmann & Voss & Co.
Trademark:	LUVOCOM®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	LaaySi_LUVOCOM-1105-7107.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
RTP 2301 A	RTP Company	PUR, Unspecified	RTP
Bayflex® 110-80 (15% Glass)	Covestro - PUR	PUR-Ether/MDI	Bayflex®
Ferro PP TPP20AC15HB-BK	Ferro Corporation	PP Homopolymer	Ferro PP
LNP™ STAT-KON™ AX02747 compound	SABIC Innovative Plastics	ABS	LNP™ STAT-KON™
LNP™ THERMOCOMP™ DX06409 compound	SABIC Innovative Plastics	PC	LNP™ THERMOCOMP™