DeWAL DW 402
| Category: | UHMWPE , Ultra High Molecular Weight Polyethylene |
| Manufacturer: | DeWAL Industries |
| Trademark: | DeWAL |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | LZb3ez_DeWAL-DW-402.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Skived Ultra High Molecular Weight Polyethylene film (UHMW) UHMW has extremely high abrasion resistance, exceeding the abrasion resistance of steel. This coupled with broad chemcial resistance and low coefficient of friction makes UHMW an extremely versatile engineering material for many severe service applications. Application examples include inner and outer surfaces for potable water, chemical, fule and hydraulic hoses, bottom surfaces for skis and snow boards as well as linings for chutes to decrease friction and wear. Automotive weather stripping. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Physical | Nominal Value | Unit | |
|---|---|---|---|
| Density | 0.930 | g/cm³ | |
| Water Absorption (Saturation) | 0.010 | % | |
| Thickness | 0.0762 to 2.36 | mm |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deformation 1(50°C) | 6.0 to 8.0 | % |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Core ID | 7.62 | cm | |
| Maximum Roll OD | 356 | mm | |
| Width 2 | 6.35 to 1220 | mm |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength - MD (Yield) | 41.4 | MPa | ASTM D882 |
| Tensile Elongation - MD (Break) | 300 | % | ASTM D882 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Annealed) | 95.0 | °C | ISO 75-2/A |
| CLTE - Flow | 2.0E-4 | cm/cm/°C | |
| Thermal Conductivity (23°C) | 0.063 | W/m/K | ASTM C177 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength | 39 | kV/mm | ASTM D149 |
| Dielectric Constant 3(1 MHz) | 2.30 | ASTM D150 | |
| Dissipation Factor | 4.0E-4 | ASTM D150 |
| Note Message | |
|---|---|
| 1 . | 2000 psi, 6 hr |
| 2 . | (increments of 1/16") |
| 3 . | 2H |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Salflex 135 | Salflex Polymers Ltd. | TPO (POE) | Salflex |
| Sinvicomp SBB3715 | Teknor Apex Asia Pacific PTE. LTD. | PVC, Rigid | Sinvicomp |
| Vipel® F085-ABB-00 | AOC, L.L.C. | Vinyl Ester | Vipel® |
| EXCELLOY CK50 | Techno Polymer Co, Ltd. | PC+ABS | EXCELLOY |
| Plasmer 1065BM/8901 | HYUNDAI EP Co., Ltd. | TPE | Plasmer |