Novalloy-A A2606
| Category: | ABS+Nylon , Acrylonitrile Butadiene Styrene + Nylon |
| Manufacturer: | PlastxWorld Inc. |
| Trademark: | Novalloy-A |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | LZTwsO_NovalloyAA2606.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Novalloy-A A2606 is an acrylonitrile butadiene styrene nylon (ABS nylon) material,. This product is available in the Asia-Pacific region,. The main characteristics of Novalloy-A A2606 are: flame retardant/rated flame. |
| General Information |
|---|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.30 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow | 0.10 - 0.50 | -- | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.60 | -- | % | ISO 62 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness (R-Scale) | 116 | 115 | ISO 2039-2 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Stress (Yield) | 120 | 95.0 | MPa | ISO 527-2 |
| Flexural Modulus | 6800 | 5500 | MPa | ISO 178 |
| Flexural Stress | 170 | 135 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 11 | -- | kJ/m² | ISO 179/1eA |
| 23°C | 16 | 18 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | ASTM D256 | |||
| -30°C, 6.40 mm | 110 | -- | J/m | ASTM D256 |
| 23°C, 6.40 mm | 160 | 190 | J/m | ASTM D256 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load | ||||
| 0.45 MPa, unannealed, 6.40mm | 215 | 210 | °C | ASTM D648 |
| 0.45 MPa, not annealed | 215 | 210 | °C | ISO 75-2/B |
| 1.8 MPa, unannealed, 6.40mm | 195 | 180 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 185 | 170 | °C | ISO 75-2/A |
| Linear thermal expansion coefficient | ISO 11359-2 | |||
| Flow | 3.0E-5 | -- | cm/cm/°C | ISO 11359-2 |
| Lateral | 1.0E-4 | -- | cm/cm/°C | ISO 11359-2 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Dielectric Strength (1.50 mm) | 14 | -- | kV/mm | ASTM D149 |
| Arc Resistance (3.00 mm) | 92.0 | -- | sec | ASTM D495 |
| Arc Resistance (3.00 mm) | PLC 6 | -- | ASTM D495 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | HB | -- | UL 94 |
| Additional Information | Dry | Conditioned | Unit | |
|---|---|---|---|---|
| Moisture Content | -- | 0.70 | % |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 - 100 | °C | |
| Drying Time | 4.0 - 5.0 | hr | |
| Rear Temperature | 180 - 210 | °C | |
| Middle Temperature | 230 - 250 | °C | |
| Front Temperature | 240 - 260 | °C | |
| Nozzle Temperature | 230 - 250 | °C | |
| Mold Temperature | 70.0 - 90.0 | °C | |
| Back Pressure | 10.0 - 20.0 | MPa | |
| Screw Speed | 50 - 80 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Teflon® PTFE 6C X | DuPont Fluoropolymers | PTFE | Teflon® PTFE |
| TEKNIFLEX® PP300 WH | Tekni-Films, a div of Tekni-Plex | Film, PP | TEKNIFLEX® |
| I. Stern 3335 | I. STERN & CO. INC. | PP Impact Copolymer | I. Stern |
| Karina IVORY PVC COMP. -E 850-35/ 1-G-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LUVOCOM® 1-8864/ES | LEHVOSS Group | Nylon 66 | LUVOCOM® |