TRILAC® ABS-HH2000
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Polymer Technology and Services, LLC |
| Trademark: | TRILAC® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | LYxoEc_TRILAC-ABS-HH2000.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
TRILAC® ABS-HH2000 is an Acrylonitrile Butadiene Styrene (ABS) product. It can be processed by injection molding and is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America. Characteristics include:
|
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.05 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 20 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 118 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 51.7 | MPa | ASTM D638 |
| Flexural Modulus | 2340 | MPa | ASTM D790 |
| Flexural Strength (Yield) | 70.3 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| 3.17 mm | 300 | J/m | |
| 6.35 mm | 270 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 96.0 | °C | |
| 1.8 MPa, Unannealed | 87.0 | °C |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.59 mm | HB | ||
| 3.17 mm | HB |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 87.8 to 93.3 | °C | |
| Drying Time | 2.0 to 24 | hr | |
| Rear Temperature | 193 | °C | |
| Middle Temperature | 216 | °C | |
| Front Temperature | 227 | °C | |
| Processing (Melt) Temp | 218 to 260 | °C | |
| Mold Temperature | 48.9 to 65.6 | °C | |
| Injection Pressure | 68.9 to 82.7 | MPa | |
| Injection Rate | Slow-Moderate | ||
| Back Pressure | 0.689 | MPa | |
| Screw Speed | 50 to 60 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PRE-ELEC® PP 1370 | Premix Oy | TPO | PRE-ELEC® |
| Axiall PVC 12842 | Axiall Corporation | PVC, Flexible | Axiall PVC |
| Jiangsu Sinarise EX7535X | Jiangsu Sinarise New Material Technology Co., Ltd | TPE | Jiangsu Sinarise |
| JSR EPR EP922P | JSR Corporation | EPDM | JSR EPR |
| LUVOCOM® 1105-8002 VP | Lehmann & Voss & Co. | PEEK | LUVOCOM® |