TORZEN® HV360AHSL NC01
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | INVISTA Engineering Polymers |
| Trademark: | TORZEN® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | LYxOVc_TORZENHV360AHSLNC01.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| TORZEN® HV360AHSL NC01 is a very high viscosity PA66 resin for extrusion and injection molding applications. It is heat stabilized and lubricated. Available in natural and black. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.14 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | ||
| Transverse flow : 2.00mm | 1.9 | % | ISO 294-4 |
| Flow : 2.00mm | 2.0 | % | ISO 294-4 |
| Water Absorption (23°C, 24 hr) | 2.1 | % | ISO 62 |
| Viscosity Number (H2SO4 (Sulphuric Acid)) | 330 | cm³/g | ISO 307 |
| Relative Viscosity | |||
| at 1% in sulfuric acid, nominal | 5 | ||
| in formic acid, nominal | 360 | ASTM D789 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3050 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 84.0 | MPa | ISO 527-2/50 |
| Tensile Strain | ISO 527-2 | ||
| Yield | 4.1 | % | ISO 527-2 |
| Fracture | 25 | % | ISO 527-2 |
| Flexural Modulus | 2900 | MPa | ISO 178 |
| Flexural Stress | 96.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -30°C | 5.0 | kJ/m² | ISO 179 |
| 23°C | 5.6 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength | ISO 179 | ||
| -30°C | No Break | ISO 179 | |
| 23°C | No Break | ISO 179 | |
| Notched Izod Impact (23°C) | 5.0 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 186 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 63.0 | °C | ISO 75-2/A |
| Melting Temperature | 261 | °C | ISO 11357-3 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.010 - 0.080 | % | |
| Rear Temperature | 250 - 270 | °C | |
| Middle Temperature | 270 - 290 | °C | |
| Front Temperature | 270 - 290 | °C | |
| Nozzle Temperature | 270 - 290 | °C | |
| Processing (Melt) Temp | 280 - 300 | °C | |
| Mold Temperature | 50 - 90 | °C | |
| Back Pressure | 0.200 - 1.00 | MPa | |
| Screw Speed | 75 - 180 | rpm | |
| Cushion | 4.00 - 6.00 | mm | |
| Vent Depth | 7.0E-3 - 0.040 | mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Radilon® AGV 25 Black | Radici Plastics | Nylon 66 | Radilon® |
| SureSpec IP-200NB | Genesis Polymers | PP Impact Copolymer | SureSpec |
| Durez® 32580 | Durez Corporation | Phenolic | Durez® |
| Karina IVORY PVC COMPOUND -E 653D35/ 1-B | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Sylvin 2990-85 Clear | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |