NORYL PPX™ PPX7200 resin
| Category: | PPE+PS+PP , Polyphenylene Ether + PS + PP |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | NORYL PPX™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | LYcG8x_NORYL-PPX-PPX7200-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PP+PPE+PS. Improved chemical resistance and surface aesthetics in injection molded applications. NSF61-capable. UL-94 HB listed. |
| General Information | |
|---|---|
| Features |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 0.988 | g/cm³ | ASTM D792 |
| -- | 0.990 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (260°C/5.0 kg) | 16 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (260°C/5.0 kg) | 18.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | Internal Method | ||
| Flow : 3.20 mm | 0.60 to 0.80 | % | |
| Across Flow : 3.20 mm | 0.60 to 0.80 | % | |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 0.050 | % | |
| Equilibrium, 23°C, 50% RH | 0.020 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 1240 | MPa | ASTM D638 |
| -- | 1670 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 33.8 | MPa | ASTM D638 |
| Yield | 34.0 | MPa | ISO 527-2/50 |
| Break 3 | 27.6 | MPa | ASTM D638 |
| Break | 28.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Yield 4 | 10 | % | ASTM D638 |
| Yield | 8.2 | % | ISO 527-2/50 |
| Break 5 | 130 | % | ASTM D638 |
| Break | 120 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| 50.0 mm Span 6 | 1450 | MPa | ASTM D790 |
| -- 7 | 1610 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 48.0 | MPa | ISO 178 |
| Yield, 50.0 mm Span 8 | 49.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 9 | ISO 179/1eA | ||
| -30°C | 6.1 | kJ/m² | |
| 23°C | 12 | kJ/m² | |
| Charpy Unnotched Impact Strength 10 | ISO 179/1eU | ||
| -30°C | 80 | kJ/m² | |
| 23°C | No Break | ||
| Notched Izod Impact | |||
| -30°C | 0.85 | J/m | ASTM D256 |
| 23°C | 150 | J/m | ASTM D256 |
| -30°C 11 | 8.0 | kJ/m² | ISO 180/1A |
| 23°C 12 | 14 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 1400 | J/m | ASTM D4812 |
| -30°C 13 | No Break | ISO 180/1U | |
| 23°C 14 | No Break | ISO 180/1U | |
| Instrumented Dart Impact (23°C, Total Energy) | 36.2 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 110 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 3.20 mm | 71.1 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 15 | 73.4 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 146 | °C | ASTM D1525 16 |
| -- | 103 | °C | ISO 306/B50 |
| -- | 107 | °C | ISO 306/B120 |
| CLTE | ASTM E831, ISO 11359-2 | ||
| Flow : -40 to 40°C | 9.9E-5 | cm/cm/°C | |
| Transverse : -40 to 40°C | 1.1E-4 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 60.0 to 65.6 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 30 to 70 | % | |
| Rear Temperature | 227 to 277 | °C | |
| Middle Temperature | 238 to 282 | °C | |
| Front Temperature | 249 to 288 | °C | |
| Nozzle Temperature | 260 to 288 | °C | |
| Processing (Melt) Temp | 260 to 288 | °C | |
| Mold Temperature | 32.2 to 48.9 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 20 to 100 | rpm | |
| Vent Depth | 0.038 to 0.051 | mm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 50 mm/min |
| 3 . | Type I, 50 mm/min |
| 4 . | Type I, 50 mm/min |
| 5 . | Type I, 50 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 80*10*4 sp=62mm |
| 10 . | 80*10*4 sp=62mm |
| 11 . | 80*10*4 |
| 12 . | 80*10*4 |
| 13 . | 80*10*4 |
| 14 . | 80*10*4 |
| 15 . | 80*10*4 mm |
| 16 . | Rate B (120°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MAXAMID™ RC66MG40-BK09 | Pier One Polymers, Inc. | Nylon 66 | MAXAMID™ |
| MAXAMID™ PA6G33IM-BK10 | Pier One Polymers, Inc. | Nylon 6 | MAXAMID™ |
| Sindustris PC SC2303 | Sincerity Australia Pty Ltd. | PC | Sindustris PC |
| K-vinyl 60 Deg C Rating Insulation (80-Wet) | Technovinyl Polymers India Ltd. | PVC, Unspecified | K-vinyl |
| POLIMAXX 1111NXTA4 | IRPC Public Company Limited | PP Homopolymer | POLIMAXX |