DAI-EL™ G-755
| Category: | Fluorelastomer , Fluoroelastomer |
| Manufacturer: | DAIKIN AMERICA, INC. |
| Trademark: | DAI-EL™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | LXtFYx_DAI-EL-G-755.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| DAI-EL G-755 is a cure-incorporated copolymer with medium Mooney viscosity. It is designed especially for extrusion molding and calendering. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | |
|---|---|---|---|
| Specific Gravity | 1.81 | g/cm³ | |
| Mooney Viscosity (ML 1+10, 121°C) | 25 | MU | |
| Fluorine Content | 66 | % |
| Hardness | Nominal Value | Unit | |
|---|---|---|---|
| Durometer Hardness | |||
| Shore A, 25°C | 70 | ||
| Shore A, 25°C 1 | 72 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | |||
| 100% Strain, 25°C | 2.80 | MPa | |
| 100% Strain, 25°C 2 | 4.30 | MPa | |
| 100% Strain, 25°C 3 | 4.40 | MPa | |
| Tensile Strength | |||
| Yield, 25°C | 10.2 | MPa | |
| Yield, 25°C 4 | 14.9 | MPa | |
| Yield, 25°C 5 | 14.7 | MPa | |
| Tensile Elongation | |||
| Break, 25°C | 410 | % | |
| Break, 25°C 6 | 260 | % | |
| Break, 25°C 7 | 250 | % | |
| Compression Set | ASTM D395 | ||
| 200°C, 70 hr | 62 | % | |
| 200°C, 70 hr 8 | 21 | % | |
| 200°C, 70 hr 9 | 24 | % |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | -18.0 | °C | ASTM D1329 |
| Note Message | |
|---|---|
| 1 . | ODR, Strain: 3°, Test time: 12 min |
| 2 . | ODR, Strain: 3°, Test time: 12 min |
| 3 . | MDR 2000, Strain: 0.5°, Test time: 6 min |
| 4 . | ODR, Strain: 3°, Test time: 12 min |
| 5 . | MDR 2000, Strain: 0.5°, Test time: 6 min |
| 6 . | ODR, Strain: 3°, Test time: 12 min |
| 7 . | MDR 2000, Strain: 0.5°, Test time: 6 min |
| 8 . | ODR, Strain: 3°, Test time: 12 min |
| 9 . | MDR 2000, Strain: 0.5°, Test time: 6 min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| THERMOLAST® K TF4CGN (Series: FC) | KRAIBURG TPE | TPE | THERMOLAST® K |
| Ultramid® B3WG6 GPX | BASF Corporation | Nylon 6 | Ultramid® |
| Elastron® D D300.D40.B | Elastron USA, Inc. | SBS | Elastron® D |
| Hostacom ERS 227N D61395 | LyondellBasell Industries | PP Copolymer | Hostacom |
| LNP™ THERMOCOMP™ RF0049S compound | SABIC Innovative Plastics | Nylon 66 | LNP™ THERMOCOMP™ |