HANWHA CHBA-8806FR
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | Hanwha Chemical |
| Trademark: | HANWHA |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | LXCDyk_HANWHA-CHBA-8806FR.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
Hanwha Wire and Cable Compound CHBA-8806FR is a low-smoke flame retardant compound. CHBA-8806FR is based on linear low density polyethylene(LLDPE) and has an excellent flame retardant properties and processability. This compound is used for jacketing of TR-CNCE-W cable.
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.30 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 3.0 | g/10 min | ASTM D1238 |
| Carbon Black Content | 2.6 | % | ASTM D1603 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 12.7 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 650 | % | ASTM D638 |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oven Aging (100°C) | 2.0 | day | |
| Tensile strength retention rate | > 90 | % | ASTM D638 |
| Elongation retention rate | > 90 | % | ASTM D638 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deformation- Thermal @100°C/2kg | % |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Light Absorption Coefficient | > 350 | Abs/mm | ASTM D3349 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | -30.0 | °C | ASTM D746 |
| Melting Temperature | 125 | °C | DSC |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Constant (1 MHz) | 3.10 | ASTM D150 | |
| Dissipation Factor (1 MHz) | 1.0E-3 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oxygen Index | > 30 | % | ASTM D2863 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 190 - 210 | °C |
| Extrusion instructions |
|---|
| Hopper Drying : 60~75°C for 3hrs |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TECOLITE KM-350(G) | KYOCERA Chemical Corporation | Phenolic | TECOLITE |
| ExxonMobil™ LLDPE LL 1001.32 | ExxonMobil Chemical | LLDPE | ExxonMobil™ LLDPE |
| LNP™ COLORCOMP™ DX98735H compound | SABIC Innovative Plastics | PC | LNP™ COLORCOMP™ |
| POLLITE 1002G20 | POLYROCKS CHEMICAL CO., LTD | PC | POLLITE |
| Axiall PVC 1651 | Axiall Corporation | PVC, Flexible | Axiall PVC |