Akulon® Ultraflow K-FKG6
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | DSM Engineering Plastics |
| Trademark: | Akulon® Ultraflow |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | LWxGtE_AkulonUltraflowKFKG6.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Akulon®Ultraflow K-FKG6 is a polyamide 6 (nylon 6) material, which contains a 30% glass fiber reinforced material. This product is available in North America or Asia Pacific,. Akulon®The main features of Ultraflow K-FKG6 are:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Forms |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.35 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Transverse flow | 1.1 | -- | % | ISO 294-4 |
| Flow | 0.30 | -- | % | ISO 294-4 |
| Water Absorption | ISO 62 | |||
| Saturated, 23°C | 6.0 | -- | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 1.8 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 9500 | 5700 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 170 | 105 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 3.5 | 7.0 | % | ISO 527-2 |
| Flexural Modulus | 8600 | -- | MPa | ISO 178 |
| Flexural Stress | 235 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 10 | 10 | kJ/m² | ISO 179/1eA |
| 23°C | 14 | 22 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 65 | 65 | kJ/m² | ISO 179/1eU |
| 23°C | 85 | 90 | kJ/m² | ISO 179/1eU |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, not annealed | 220 | -- | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 210 | -- | °C | ISO 75-2/A |
| Melting Temperature 1 | 220 | -- | °C | ISO 11357-3 |
| Linear thermal expansion coefficient | ISO 11359-2 | |||
| Flow | 2.0E-5 | -- | cm/cm/°C | ISO 11359-2 |
| Lateral | 7.0E-5 | -- | cm/cm/°C | ISO 11359-2 |
| Flammability | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| Flammability Classification (1.6 mm) | HB | -- | IEC 60695-11-10, -20 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80 | °C | |
| Drying Time | 4.0 - 8.0 | hr | |
| Rear Temperature | 230 - 250 | °C | |
| Middle Temperature | 230 - 260 | °C | |
| Front Temperature | 230 - 260 | °C | |
| Nozzle Temperature | 250 - 280 | °C | |
| Processing (Melt) Temp | 245 - 270 | °C | |
| Mold Temperature | 40 - 80 | °C | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 3.00 - 10.0 | MPa | |
| Screw Compression Ratio | 2.5:1.0 |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sumitomo Epoxy TEM 9053C | Sumitomo Bakelite North America, Inc. | Epoxy | Sumitomo Epoxy |
| ALTECH® PA66 C 1000/506 | ALBIS PLASTIC GmbH | Nylon 66 | ALTECH® PA66 |
| Geon™ Vinyl Rigid Extrusion 87150 | PolyOne Corporation | PVC, Rigid | Geon™ Vinyl Rigid Extrusion |
| MAJ'ECO GP130 CEL | AD majoris | Biodeg Polymers | MAJ'ECO |
| PLEXIGLAS® Sheet Resist 75 | Evonik Industries AG | Acrylic (PMMA) | PLEXIGLAS® Sheet |