Badalac® ABS 20 HH
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Bada AG |
| Trademark: | Badalac® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | LWx04a_Badalac-ABS-20-HH.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Injection moulding grade, high resistance to heat deformation, high impact resistance |
| General Information | |
|---|---|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.04 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (220°C/10.0 kg) | 7.00 | cm³/10min | ISO 1133 |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 1.0 | % | |
| Equilibrium, 23°C, 50% RH | 0.22 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 2400 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield, 23°C) | 51.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Yield, 23°C) | 3.0 | % | ISO 527-2/50 |
| Nominal Tensile Strain at Break (23°C) | 9.0 | % | ISO 527-2/50 |
| Flexural Stress 1(23°C) | 72.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 2 | ISO 179/1eA | ||
| -30°C | 7.0 | kJ/m² | |
| 23°C | 17 | kJ/m² | |
| Charpy Unnotched Impact Strength 3 | ISO 179/1eU | ||
| -30°C | 100 | kJ/m² | |
| 23°C | 190 | kJ/m² | |
| Notched Izod Impact Strength 4(23°C) | 19 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 5 | |||
| 0.45 MPa, Unannealed | 111 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 106 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 112 | °C | ISO 306/A50 |
| -- | 106 | °C | ISO 306/B50 |
| CLTE - Flow 6 | 8.0E-5 to 1.1E-4 | cm/cm/°C | DIN 53752 |
| Maximum Service Temperature - 20000 hrs | 90 | °C | IEC 216 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity 7 | 1.0E+13 | ohms | IEC 60093 |
| Volume Resistivity 8 | 1.0E+13 | ohms·cm | IEC 60093 |
| Electric Strength 9 | 37 | kV/mm | IEC 60243-1 |
| Relative Permittivity 10(1 MHz) | 2.80 | IEC 60250 | |
| Dissipation Factor 11(1 MHz) | 7.9E-3 | IEC 60250 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.800 mm 12 | HB | ||
| 1.60 mm 13 | HB |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Processing (Melt) Temp | 220 to 260 | °C | |
| Mold Temperature | 30.0 to 60.0 | °C |
| Note Message | |
|---|---|
| 1 . | 80x10x4 mm |
| 2 . | 80x10x4 mm |
| 3 . | 80x10x4 mm |
| 4 . | 80x10x4 mm |
| 5 . | 110x10x4 mm |
| 6 . | >=10x10x4 mm |
| 7 . | 80x80x1 mm |
| 8 . | 80x80x1 mm |
| 9 . | 80x80x1 mm |
| 10 . | 80x80x1 mm |
| 11 . | 80x80x1 mm |
| 12 . | 125x13x0.8 mm |
| 13 . | 125x13x1.6 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Novalloy-B B5746 (Type J) | Daicel Polymer Ltd. | ABS+PBT | Novalloy-B |
| Adell Polyamide AR-18 | Adell Plastics, Inc. | Nylon 66 | Adell Polyamide |
| Alcryn® 4680 NC | Advanced Polymer Alloys | MPR | Alcryn® |
| BP Flex D 6017 T BLK | Buckeye Polymers, Inc. | TPO | BP Flex |
| Fireguard® 910L16-C13-NL | Teknor Apex Company | PVC, Flexible | Fireguard® |