Category: | PP, Unspecified , Polypropylene |
Manufacturer: | Borealis AG |
Trademark: | Borealis PP |
Fillers: | - |
Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
Delivery Terms | FOB, CIF, DAP, DAT, DDP |
PDF: | LWDY2P_Borealis-PP-EE106AEB.pdf ![]() |
PRICE: | Order Products email sales@su-jiao.com |
Message |
---|
EE106AEB is a 15% mineral reinforced impact modified polypropylene compound suitable for injection moulding. |
General Information | |
---|---|
Filler / Reinforcement |
|
Additive |
|
Features |
|
Uses |
|
Physical | Nominal Value | Unit | Test Method |
---|---|---|---|
Density (23°C) | 0.992 | g/cm³ | ISO 1183 |
Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 15 | g/10 min | ISO 1133 |
Mechanical | Nominal Value | Unit | Test Method |
---|---|---|---|
Flexural Modulus 1 | 1660 | MPa | ISO 178 |
Flexural Stress | 28.0 | MPa | ISO 178 |
Impact | Nominal Value | Unit | Test Method |
---|---|---|---|
Notched Izod Impact | ISO 180/1A | ||
0°C | 5.5 | kJ/m² | ISO 180/1A |
23°C | 18 | kJ/m² | ISO 180/1A |
Thermal | Nominal Value | Unit | Test Method |
---|---|---|---|
Heat Deflection Temperature (1.8 MPa, Unannealed) | 55.0 | °C | ISO 75-2/Ae |
Vicat Softening Temperature | 52.0 | °C | ISO 306/B50 |
Flammability | Nominal Value | Unit | Test Method |
---|---|---|---|
Flammability | 100 | mm/min | ISO 3795 |
Injection | Nominal Value | Unit | |
---|---|---|---|
Mold Temperature | 30.0 - 50.0 | °C | |
Holding Pressure | 30.0 - 60.0 | MPa |
Injection instructions |
---|
Feeding Temperature: 40 - 80 °CMass Temperature: 220 - 260 °CBack Pressure: Low to MediumScrew Speed: Low to MediumFlow Front Speed: 100 - 200 mm/s |
Note Message | |
---|---|
1 . | 2.0 mm/min |
Resin Grade | Manufacturer | Category | Trademark |
---|---|---|---|
Rhelon G2533H-01A | RheTech, Inc. | Nylon 66 | Rhelon |
SCHULAFORM® 9 E HI | A. Schulman Europe | Acetal (POM) Copolymer | SCHULAFORM® |
Sinvicomp SGH6020 | Teknor Apex Asia Pacific PTE. LTD. | PVC, Flexible | Sinvicomp |
Hifax 7430P | LyondellBasell Industries | TPO (POE) | Hifax |
LNP™ LUBRILOY™ KL201 compound | SABIC Innovative Plastics | Acetal (POM) Copolymer | LNP™ LUBRILOY™ |