Smoothblend® PC-1302
| Category: | PC , Polycarbonate |
| Manufacturer: | Colour Image Plastic Compound Sdn. Bhd. (CIPC) |
| Trademark: | Smoothblend® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | LVtRIe_Smoothblend-PC-1302.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Smoothblend® PC-1302 is a wear resistance polycarbonate compound offering superb lubricity by incorporating PTFE and carbon fiber. It is developed for applications demanding stringent wear resistant and low friction performance. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.55 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.20 mm) | 0.10 to 0.30 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 115 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 2.0 | % | ASTM D638 |
| Flexural Modulus | 8610 | MPa | ASTM D790 |
| Flexural Strength | 180 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 190 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 4.00 mm) | 145 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Rear Temperature | 275 to 280 | °C | |
| Middle Temperature | 280 to 285 | °C | |
| Front Temperature | 285 to 290 | °C | |
| Nozzle Temperature | 290 to 295 | °C | |
| Processing (Melt) Temp | 275 to 300 | °C | |
| Mold Temperature | 85.0 to 110 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PTS PCA-2201NH | Polymer Technology and Services, LLC | PC+ABS | PTS |
| Tufpet PBT N2800 | Mitsubishi Rayon America Inc. | PBT | Tufpet |
| AIE PA66 60G6 | Asia International Enterprise (Hong Kong) Limited | Nylon 66 | AIE PA66 |
| EVALENE® HDPE HB33531 | JG Summit Petrochemical Corporation | HDPE | EVALENE® HDPE |
| LG PS 20HR(E) | LG Chem Ltd. | PS (HIPS) | LG PS |