LNP™ THERMOCOMP™ RF0069S compound
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | LUlGmh_LNP-THERMOCOMP-RF0069S-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP* RF0069S is a compound based on Nylon 66 resin containing 30% Glass Fiber. Added features of this material include: Flame Retardant, Heat Stabilized. Also known as: LNP* THERMOCOMP* Compound RF-1006 FR HS Product reorder name: RF0069S |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.71 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 0.30 | % | |
| Across Flow : 24 hr | 1.0 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 165 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 2.7 | % | ASTM D638 |
| Flexural Modulus | 12200 | MPa | ASTM D790 |
| Flexural Strength | 241 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 75 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 690 | J/m | ASTM D4812 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 to 0.25 | % | |
| Rear Temperature | 266 to 277 | °C | |
| Middle Temperature | 282 to 293 | °C | |
| Front Temperature | 293 to 304 | °C | |
| Processing (Melt) Temp | 277 to 288 | °C | |
| Mold Temperature | 82.2 to 93.3 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 6221-83 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| CompaDur® 121 black (018) | DimeLika Plast GmbH | PBT | CompaDur® |
| Elastocon® 8088BL | Elastocon TPE Technologies | TPE | Elastocon® |
| Karina WHITE PVC COMPOUND 850-10/1-F-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LUVOCOM® 1880-8821 | Lehmann & Voss & Co. | LCP | LUVOCOM® |