VALOX™ DR48 resin

Category:	PBT , Polybutylene Terephthalate
Manufacturer:	SABIC Innovative Plastics
Trademark:	VALOX™
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	LUB4ts_VALOX-DR48-resin.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message
17% glass reinforced, flame retardant grade UL-94 rated V-0/5VA.

General Information
Filler / Reinforcement	Glass Fiber, 17% Filler by Weight
Features	Flame Retardant
Processing Method	Injection Molding
Multi-Point Data	Coefficient of Thermal Expansion vs. Temperature (ASTM E831) Elastic Modulus vs Temperature (ASTM D4065) Flexural DMA (ASTM D4065) Pressure-Volume-Temperature (PVT - Zoller Method) Shear DMA (ASTM D4065) Specific Heat vs. Temperature (ASTM D3417) Tensile Creep (ASTM D2990) Tensile Fatigue Tensile Stress vs. Strain (ASTM D638) Thermal Conductivity vs. Temperature (ASTM E1530) Viscosity vs. Shear Rate (ASTM D3835)

Physical	Nominal Value	Unit	Test Method
Specific Gravity	1.53	g/cm³	ASTM D792
Specific Volume	0.660	cm³/g	ASTM D792
Molding Shrinkage			Internal Method
Flow ¹	0.60 to 0.90	%
Flow ²	0.40 to 0.60	%
Across Flow ³	0.50 to 0.80	%
Across Flow ⁴	0.80 to 1.1	%
Water Absorption (24 hr)	0.070	%	ASTM D570

Hardness	Nominal Value	Unit	Test Method
Rockwell Hardness (R-Scale)	118		ASTM D785

Mechanical	Nominal Value	Unit	Test Method
Tensile Strength ⁵(Break)	93.1	MPa	ASTM D638
Flexural Modulus ⁶(50.0 mm Span)	5030	MPa	ASTM D790
Flexural Strength ⁷(Break, 50.0 mm Span)	145	MPa	ASTM D790

Impact	Nominal Value	Unit	Test Method
Notched Izod Impact (23°C)	53	J/m	ASTM D256
Unnotched Izod Impact (23°C)	530	J/m	ASTM D4812

Thermal	Nominal Value	Unit	Test Method
Deflection Temperature Under Load			ASTM D648
0.45 MPa, Unannealed, 6.40 mm	210	°C
1.8 MPa, Unannealed, 6.40 mm	182	°C
Ball Pressure Test (125°C)	Pass		IEC 60695-10-2
CLTE - Flow			ASTM E831
-40 to 40°C	2.0E-5	cm/cm/°C
60 to 138°C	2.0E-5	cm/cm/°C
RTI Elec	120	°C	UL 746
RTI Imp	120	°C	UL 746
RTI Str	140	°C	UL 746

Electrical	Nominal Value	Unit	Test Method
Volume Resistivity	3.6E+16	ohms·cm	ASTM D257
Dielectric Strength			ASTM D149
1.60 mm, in Oil	26	kV/mm
3.20 mm, in Air	19	kV/mm
Dielectric Constant			ASTM D150
100 Hz	3.60
1 MHz	3.40
Dissipation Factor			ASTM D150
100 Hz	2.0E-3
1 MHz	0.020
Arc Resistance ⁸	PLC 6		ASTM D495
Comparative Tracking Index (CTI)	PLC 3		UL 746
High Amp Arc Ignition (HAI)	PLC 0		UL 746
High Voltage Arc Tracking Rate (HVTR)	PLC 4		UL 746
Hot-wire Ignition (HWI)	PLC 3		UL 746

Flammability	Nominal Value	Unit	Test Method
Flame Rating			UL 94
0.890 mm	V-0
3.00 mm	5VA
Glow Wire Flammability Index			IEC 60695-2-12
1.00 mm	960	°C
3.00 mm ⁹	960	°C
Glow Wire Ignition Temperature			IEC 60695-2-13
1.00 mm	700	°C
3.00 mm	725	°C
Oxygen Index	29	%	ASTM D2863

Injection	Nominal Value	Unit
Drying Temperature	121	°C
Drying Time	3.0 to 4.0	hr
Drying Time, Maximum	12	hr
Suggested Max Moisture	0.020	%
Suggested Shot Size	40 to 80	%
Rear Temperature	238 to 254	°C
Middle Temperature	243 to 260	°C
Front Temperature	249 to 266	°C
Nozzle Temperature	243 to 260	°C
Processing (Melt) Temp	249 to 266	°C
Mold Temperature	65.6 to 87.8	°C
Back Pressure	0.345 to 0.689	MPa
Screw Speed	50 to 80	rpm
Vent Depth	0.025 to 0.038	mm

Note Message
1 .	3.2 to 4.6 mm
2 .	1.5 to 3.2 mm
3 .	1.5 to 3.2 mm
4 .	3.2-4.6 mm
5 .	Type I, 5.0 mm/min
6 .	1.3 mm/min
7 .	1.3 mm/min
8 .	Tungsten Electrode
9 .	by VDE

Resin Grade	Manufacturer	Category	Trademark
Spartech Polycom SC7-7006	Spartech Polycom	PC	Spartech
VENYL ST228 - 7935	AD majoris	Nylon 6	VENYL
Generic LCP - Glass\Mineral	Generic	LCP	Generic
Karina IVORY PVC COMPOUND 70900-35/1-F-AC-LMP	Karina Ind. e Com. de Plásticos Ltda	PVC, Unspecified	Karina
Neoflex™ 8085	Zylog Plastalloys Pvt. Ltd.	TPE	Neoflex™