Vacuum Cast V-825 A/B
| Category: | TSU , Polyurethane Thermoset Elastomer |
| Manufacturer: | BJB Enterprises, Inc. |
| Trademark: | Vacuum Cast |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | LU6MlR_Vacuum-Cast-V-825-A-B.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| V-825 A/B is a rigid 84 Shore D polyurethane system that exhibits exceptional physical properties. It is a high performance material that features high heat deflection capability and a low shrink factor. V-825 is a transparent, virtually colorless casting material that allows for unrestricted tinting and precise color matching. This product is ideal for producing intrinsically colored parts requiring a non-painted finish. This product can be easily processed with meter-mix-dispense, pressure or vacuum cast equipment. |
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (12.7 mm) | 0.10 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 84 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2280 | MPa | ASTM D638 |
| Tensile Strength | 69.4 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 11 | % | ASTM D638 |
| Flexural Modulus | 2480 | MPa | ASTM D790 |
| Flexural Strength | 94.5 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 61 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 87.8 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 76.7 | °C | ASTM D648 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Mix Viscosity (25°C) | 450 | cP | ASTM D2393 |
| Demold Time (25°C) | 120 - 180 | min | |
| Post Cure Time (52°C) | 2.0 - 4.0 | hr |
| Additional Information |
|---|
| Mix ratio by weight: 100/60Mix ratio by volume: 100/66Work time, 100 g, 77°F: 6-8 minGel Time: 7-9 min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| VITAMIDE® AS10VN6543 | Jackdaw Polymers | Nylon 66 | VITAMIDE® |
| NuSil CV1-1142 | NuSil Technology | Silicone | NuSil |
| Braskem PP C705-44NAHP | Braskem Europe GmbH | PP Impact Copolymer | Braskem PP |
| Hanwha Total PP RP100 | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP, Unspecified | Hanwha Total PP |
| Pujie CPE230A | Zhanhua Pujie Chemical Technology Co.,Ltd | CPE | Pujie |