Radilon® S RV150 100 NAT
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Radici Plastics |
| Trademark: | Radilon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | LTN7my_Radilon-S-RV150-100-NAT.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PA6 15% glass fiber reinforced injection moulding grade. Natural colour. Suitable for parts requiring improved stiffness. ISO 1043 : PA6 GF15 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.20 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage 1 | ISO 294-4 | |||
| Across Flow | 0.80 | -- | % | |
| Flow | 0.50 | -- | % | |
| Water Absorption | ISO 62 | |||
| Saturation, 23°C, 2.00 mm | 8.5 | -- | % | |
| Equilibrium, 23°C, 2.00 mm, 50% RH | 2.5 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 5800 | 3800 | MPa | ISO 527-2/1A/1 |
| Tensile Stress | ||||
| Yield | -- | 80.0 | MPa | ISO 527-2/1A/50 |
| Break | 130 | -- | MPa | ISO 527-2/1A/5 |
| Tensile Strain | ||||
| Yield | -- | 4.0 | % | ISO 527-2/1A/50 |
| Break | 3.8 | -- | % | ISO 527-2/1A/5 |
| Nominal Tensile Strain at Break | -- | 10 | % | ISO 527-2/1A/50 |
| Flexural Modulus 2 | 5200 | -- | MPa | ISO 178 |
| Flexural Stress 3 | 190 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 5.5 | -- | kJ/m² | |
| 23°C | 7.0 | 10 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 40 | -- | kJ/m² | |
| 23°C | 45 | 70 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 190 | -- | °C | ISO 75-2/Af |
| Vicat Softening Temperature | 205 | -- | °C | ISO 306/B50 |
| Melting Temperature 4 | 220 | -- | °C | ISO 11357 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+12 | 1.0E+10 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | 1.0E+13 | ohms·cm | IEC 60093 |
| Comparative Tracking Index | 600 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Rate | 0.0 | -- | mm/min | FMVSS 302 |
| Flame Rating (0.800 mm) | HB | -- | UL 94 | |
| Glow Wire Flammability Index (2.00 mm) | 700 | -- | °C | IEC 60695-2-12 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature - Desiccant Dryer | 80.0 | °C | |
| Drying Time - Desiccant Dryer | 2.0 to 4.0 | hr | |
| Dew Point - Desiccant Dryer | < -20.0 | °C | |
| Suggested Max Moisture | 0.15 | % | |
| Processing (Melt) Temp | 240 to 280 | °C | |
| Mold Temperature | 80.0 to 90.0 | °C | |
| Injection Rate | Moderate-Fast |
| Note Message | |
|---|---|
| 1 . | 280°C Melt Temp / 80°C Mold Temp / 30 Mpa Cavity press |
| 2 . | 2.0 mm/min |
| 3 . | 2.0 mm/min |
| 4 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| DESLON™ 66 DSC201SM2 | DESCO Co., Ltd. | Nylon 66 | DESLON™ 66 |
| Geon™ Vinyl Flexible XV3785 | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Flexible |
| LEXAN™ EX9332T resin | SABIC Innovative Plastics Europe | PC | LEXAN™ |
| Sylvin 5170-85 Red 6222 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Kepamid® 1325GVS | Korea Engineering Plastics Co., Ltd | Nylon 6 | Kepamid® |