Strator® C-5
| Category: | TP, Unspecified , Polyamide 66 |
| Manufacturer: | EPIC Polymers |
| Trademark: | Strator® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | LSksP9_Strator-C-5.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| STRATOR®C- 5 is a thermoplastic product that contains 50% long glass fibers as filler. It is available in Europe. The main characteristics are: high strength. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Forms |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.60 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow | 0.20 | -- | % | ISO 294-4 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 1.5 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | ISO 527-2 | |||
| 23°C | 18000 | 14000 | MPa | ISO 527-2 |
| 90°C | 10500 | -- | MPa | ISO 527-2 |
| 120°C | 8500 | -- | MPa | ISO 527-2 |
| Tensile Stress | ISO 527-2 | |||
| Fracture, 23°C | 260 | 205 | MPa | ISO 527-2 |
| Fracture, 90°C | 210 | -- | MPa | ISO 527-2 |
| Fracture, 120°C | 140 | -- | MPa | ISO 527-2 |
| Tensile Strain (Break) | 2.2 | -- | % | ISO 527-2 |
| Flexural Modulus (23°C) | 15500 | 12000 | MPa | ISO 178 |
| Flexural Stress (23°C) | 415 | 325 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 35 | 36 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 81 | 100 | kJ/m² | ISO 179 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, not annealed | 245 | -- | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 237 | -- | °C | ISO 75-2/A |
| CLTE - Flow | 2.0E-5 | -- | cm/cm/°C | ISO 7991 |
| Thermal Conductivity | 0.33 | -- | W/m/K | ISO 22007 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+12 | -- | ohms | ASTM D257 |
| Dielectric Strength (2.00 mm) | 36 | -- | kV/mm | IEC 60243-1 |
| Comparative Tracking Index | 500 | -- | V | IEC 60112 |
| Additional Information |
|---|
| 干燥 The value listed as Molding Shrinkage ISO 294-4, was tested in accordance with S.O.P. methods. |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 110 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.10 | % | |
| Rear Temperature | 270 - 300 | °C | |
| Middle Temperature | 270 - 300 | °C | |
| Front Temperature | 285 - 310 | °C | |
| Nozzle Temperature | 285 - 320 | °C | |
| Processing (Melt) Temp | < 310 | °C | |
| Mold Temperature | 80.0 - 160 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Mar-Bal MB1000-PC | Mar-Bal, Inc. | Polyester, TP | Mar-Bal |
| Radilon® S 40 EPT2808 333 NER | Radici Plastics | Nylon 6 | Radilon® |
| Siloxane Masterbatch MB25-501 | Multibase, A Dow Corning Company | Siloxane, UHMW | Siloxane Masterbatch |
| ELASTOSIL® R plus 4001/50 | Wacker Chemie AG | Silicone | ELASTOSIL® R plus |
| Karina RED PVC COMPOUND TR-500D42/225-B-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |