Reny® G07S
| Category: | PARA , Polyarylamide |
| Manufacturer: | Mitsubishi Engineering-Plastics Corp |
| Trademark: | Reny® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | LRD59L_Reny-G07S.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Reny® G07S is a Polyarylamide (PARA) material filled with 20% glass fiber. It is available in Asia Pacific, Europe, or North America for injection molding. Important attributes of Reny® G07S are:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.52 | -- | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (275°C/2.16 kg) | 16 | -- | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (275°C/2.16 kg) | 10.9 | -- | cm³/10min | ISO 1133 |
| Molding Shrinkage | 0.43 | -- | % | |
| Water Absorption | ISO 62 | |||
| Saturation, 23°C | 0.13 | -- | % | |
| Equilibrium, 23°C, 50% RH | 1.1 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 9200 | 9100 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 155 | 136 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 2.5 | 2.5 | % | ISO 527-2 |
| Flexural Modulus | 9000 | 8900 | MPa | ISO 178 |
| Flexural Stress | 230 | 200 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 6.0 | 5.9 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 38 | 37 | kJ/m² | ISO 179 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 255 | 251 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 236 | 227 | °C | ISO 75-2/A |
| Flammability | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| Flame Rating (1.60 mm) | HB | -- | UL 94 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| A | 120 | °C | |
| B | 80.0 | °C | |
| Drying Time | |||
| A | > 3.0 | hr | |
| B | > 12 | hr | |
| Rear Temperature | 275 | °C | |
| Middle Temperature | 280 | °C | |
| Front Temperature | 285 | °C | |
| Nozzle Temperature | 285 | °C | |
| Mold Temperature | 120 to 140 | °C | |
| Injection Pressure | 20.0 to 150 | MPa | |
| Injection Rate | Moderate-Fast | ||
| Screw Speed | 60 to 150 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Braskem PP C144-04NA | Braskem America Inc. | PP Impact Copolymer | Braskem PP |
| ANYPOL SE-2000P | SH Energy & Chemical | PS (EPS) | ANYPOL |
| Hostacom EP Q 40 RN/6 | LyondellBasell Industries | PP, Unspecified | Hostacom |
| Optital 900C | The Materials Group | Acetal (POM) Copolymer | Optital |
| Sylvin 4250-50 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |