Crastin® LW9020FR NC010
| Category: | PBT , THERMOPLASTIC POLYESTER RESIN |
| Manufacturer: | DuPont Performance Polymers |
| Trademark: | Crastin® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | LQtYdV_Crastin-LW9020FR-NC010.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 20% Glass Reinforced, Flame Retardant, Polybutylene Terephthalate Blend with Low Warpage Characteristics |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Multi-Point Data |
|
| Part Marking Code (ISO 11469) |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.52 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow | 0.80 | % | |
| Flow | 0.40 | % | |
| Water Absorption | ISO 62 | ||
| 23°C, 24 hr, 2.00 mm | 0.78 | % | |
| Equilibrium, 23°C, 2.00 mm, 50% RH | 0.23 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 8500 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 110 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 2.0 | % | ISO 527-2 |
| Tensile Creep Modulus | ISO 899-1 | ||
| 1 hr | 7500 | MPa | |
| 1000 hr | 6000 | MPa | |
| Flexural Stress | 155 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 6.5 | kJ/m² | |
| 23°C | 7.0 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 35 | kJ/m² | |
| 23°C | 40 | kJ/m² | |
| Notched Izod Impact Strength | ISO 180/1A | ||
| -30°C | 6.0 | kJ/m² | |
| 23°C | 6.0 | kJ/m² | |
| Unnotched Izod Impact Strength | ISO 180/1U | ||
| -30°C | 33 | kJ/m² | |
| 23°C | 33 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 215 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 175 | °C | ISO 75-2/A |
| Melting Temperature 1 | 225 | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | ||
| Flow | 3.0E-5 | cm/cm/°C | |
| Transverse | 1.0E-4 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+14 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+15 | ohms·cm | IEC 60093 |
| Electric Strength | |||
| -- | 29 | kV/mm | IEC 60243-1 |
| 1.00 mm 2 | 29 | kV/mm | IEC 60243-1 |
| 2.00 mm 3 | 20 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | ||
| 100 Hz | 3.70 | ||
| 1 MHz | 3.50 | ||
| Dissipation Factor | ASTM D150, IEC 60250 | ||
| 100 Hz | 3.0E-3 | ||
| 1 MHz | 0.015 | ||
| Comparative Tracking Index | 300 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flammability Classification (1.50 mm) | V-0 | IEC 60695-11-10, -20 | |
| Oxygen Index | 27 | % | ISO 4589-2 |
| Fill Analysis | Nominal Value | Unit | |
|---|---|---|---|
| Melt Density | 1.36 | g/cm³ | |
| Specific Heat Capacity of Melt | 1900 | J/kg/°C | |
| Thermal Conductivity of Melt | 0.25 | W/m/K |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| 2 . | Short Time |
| 3 . | 20 sec |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 2099 X 134503 A | RTP Company | PLA | RTP |
| Sarlink® TPE ME-2245B BLK X (PRELIMINARY DATA) | Teknor Apex Company | TPE | Sarlink® TPE |
| Advanced Composites BJS-MNR2 | Advanced Composites, Inc. | PP, Unspecified | Advanced Composites |
| KOPLA PC KCP1000F | KOPLA Co., Ltd. | PC | KOPLA PC |
| Daelim Po1y® XP3200H | DAELIM INDUSTRIAL CO., LTD. | mLLDPE | Daelim Po1y® |