Valtra® MC3100
| Category: | PS (GPPS) , General Purpose Polystyrene |
| Manufacturer: | Saudi Polymers Company |
| Trademark: | Valtra® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | LQc8xB_Valtra-MC3100.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
Features
Typical Applications
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.04 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) | 3.0 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1(3.20 mm, Injection Molded) | 3170 | MPa | ASTM D638 |
| Tensile Strength 2 | ASTM D638 | ||
| Yield, 3.20 mm, Injection Molded | 54.0 | MPa | |
| Break, 3.20 mm, Injection Molded | 54.0 | MPa | |
| Tensile Elongation 3(Yield, 3.20 mm, Injection Molded) | 4.5 | % | ASTM D638 |
| Flexural Modulus 4(3.20 mm, Injection Molded) | 3100 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| 23°C, 3.18 mm | 19 | J/m | |
| 23°C, 6.35 mm | 13 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 107 | °C | ASTM D1525 5 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 5.0 mm/min |
| 4 . | 2.5 mm/min |
| 5 . | Rate B (120°C/h) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Moplen HP564R | LyondellBasell Industries | PP Homopolymer | Moplen |
| Toraypef® 15020 AP01 | Toray Resin Company | Polyolefin, Unspecified | Toraypef® |
| apigo® 8376 BS/70 | API SpA | TPO (POE) | apigo® |
| Cri-Line FDA-618-BR | Cri-Tech, Inc. | Fluorelastomer | Cri-Line |
| LNP™ THERMOCOMP™ RF006LXP compound | SABIC Innovative Plastics Asia Pacific | Nylon 66 | LNP™ THERMOCOMP™ |