LNP™ LUBRILOY™ RF203AXH compound
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRILOY™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | LQYMQw_LNP-LUBRILOY-RF203AXH-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRILOY RF203AXH is a compound based on Nylon 66 resin containing 15% Glass Fiber, Proprietary Lubricant. Added features of this material include: Wear Resistant, Healthcare. Also known as: LNP* LUBRILOY* Compound RF-15 HC Product reorder name: RF203AXH |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.12 | g/cm³ | ASTM D792 |
| -- | 1.13 | g/cm³ | ISO 1183, ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 0.80 to 1.0 | % | |
| Across Flow : 24 hr | 1.0 to 3.0 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.40 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.60 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | ASTM D638 | ||
| -- 1 | 5040 | MPa | |
| -- 2 | 4890 | MPa | |
| Tensile Strength | |||
| Break 3 | 87.0 | MPa | ASTM D638 |
| Break | 90.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Break 4 | 3.7 | % | ASTM D638 |
| Break | 3.8 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 5 | 4180 | MPa | ASTM D790 |
| -- 6 | 5500 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 140 | MPa | ISO 178 |
| Yield, 50.0 mm Span 7 | 136 | MPa | ASTM D790 |
| Break, 50.0 mm Span 8 | 128 | MPa | ASTM D790 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| vs. Itself - Dynamic | 0.37 0.36 | ||
| vs. Itself - Static | 0.40 0.30 | ||
| Wear Factor | ASTM D3702 Modified | ||
| Ring | 3.00 | 10^-10 in^5-min/ft-lb-hr | |
| Washer | 44.0 70.0 | 10^-10 in^5-min/ft-lb-hr |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 83 | J/m | ASTM D256 |
| 23°C 9 | 9.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 650 | J/m | ASTM D4812 |
| 23°C 10 | 30 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Total Energy | 11.0 | J | ASTM D3763 |
| -- | 2.80 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 252 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 11 | 244 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 238 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 12 | 232 | °C | ISO 75-2/Af |
| CLTE | ASTM D696 | ||
| Flow : -30 to 30°C | 5.6E-5 | cm/cm/°C | |
| Transverse : -30 to 30°C | 1.0E-6 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 to 0.25 | % | |
| Rear Temperature | 266 to 277 | °C | |
| Middle Temperature | 282 to 293 | °C | |
| Front Temperature | 293 to 304 | °C | |
| Processing (Melt) Temp | 271 to 282 | °C | |
| Mold Temperature | 82.2 to 93.3 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 50 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | 1.3 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 1.3 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 80*10*4 |
| 10 . | 80*10*4 |
| 11 . | 80*10*4 mm |
| 12 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Spartech Polycom SCR2-1085 | Spartech Polycom | PS (GPPS) | Spartech |
| STAR-THERM® WG B-1 | EPIC Polymers | Nylon 6 | STAR-THERM® |
| Sylvin 8280-80 Natural | Sylvin Technologies Incorporated | PVC, Flexible | Sylvin |
| Ultra Low Outgassing™ SCV1-2590 | NuSil Technology | Silicone | Ultra Low Outgassing™ |
| LEXAN™ LUX9132C resin | SABIC Innovative Plastics | PC | LEXAN™ |