LNP™ COLORCOMP™ G1000 compound
| Category: | PSU , Polysulfone |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ COLORCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | LOxzyl_LNP-COLORCOMP-G1000-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP COLORCOMP G1000 is an unfilled Polysulfone resin. Added feature of this grade is: Transparent. Also known as: LNP* COLORCOMP* Compound G-1000 Product reorder name: G1000 |
| General Information | |
|---|---|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.24 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (24 hr) | 0.70 | % | ASTM D955 |
| Water Absorption (24 hr, 50% RH) | 0.30 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 2480 | MPa | ASTM D638 |
| Tensile Strength 2(Break) | 70.3 | MPa | ASTM D638 |
| Tensile Elongation 3(Break) | 50 to 100 | % | ASTM D638 |
| Flexural Modulus 4(50.0 mm Span) | 2690 | MPa | ASTM D790 |
| Flexural Strength 5(Yield, 50.0 mm Span) | 106 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 69 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.20 mm) | 174 | °C | ASTM D648 |
| CLTE - Flow (-30 to 30°C) | 5.6E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 3.0E+17 | ohms·cm | ASTM D257 |
| Dissipation Factor | ASTM D150 | ||
| 50 Hz | 7.0E-4 | ||
| 60 Hz | 7.0E-4 | ||
| 1 kHz | 1.0E-3 | ||
| 1 MHz | 6.0E-3 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 to 149 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.050 | % | |
| Rear Temperature | 327 to 338 | °C | |
| Middle Temperature | 338 to 349 | °C | |
| Front Temperature | 349 to 360 | °C | |
| Processing (Melt) Temp | 360 to 371 | °C | |
| Mold Temperature | 149 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shinko-Lac® ASA S610 | Mitsubishi Rayon America Inc. | ASA | Shinko-Lac® |
| SILVER® F-1 | Guangdong Silver Age Sci & Tech. Co., Ltd | PVC, Unspecified | SILVER® |
| KRATON® G1643 M | Kraton Polymers LLC | SEBS | KRATON® |
| Ixan® PVS 706 | Solvay Specialty Polymers | PVDC | Ixan® |
| Sylvin 3210-85 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |