Durethan® DP AKV 30 FN00 000000

Category:	Nylon 66 , Polyamide 66
Manufacturer:	LANXESS GmbH
Trademark:	Durethan®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	LOBQHE_DurethanDPAKV30FN00000000.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message
PA 66, 30 % glass fibers, injection molding, halogen free flame retardant

General Information
Filler / Reinforcement	Glass fiber reinforced material, 30% filler by weight
Additive	Flame retardancy
Features	Halogen-free Flame retardancy
Agency Ratings	EC 1907/2006 (REACH)
Processing Method	Injection molding
Resin ID (ISO 1043)	PA GF FR (30+40)

Physical	Dry	Conditioned	Unit	Test Method
Density (23°C)	1.42	--	g/cm³	ISO 1183
Molding Shrinkage				ISO 2577
Vertical flow direction : 270°C, 2.00mm ¹	0.70	--	%	ISO 2577
Vertical flow direction : 120°C, 4 hours, 2.00mm ²	0.10	--	%	ISO 2577
Flow direction : 270°C, 2.00mm ³	0.20	--	%	ISO 2577
Flow direction : 120°C, 4 hours, 2.00mm ⁴	0.10	--	%	ISO 2577
Water Absorption				ISO 62
Saturated, 23°C	4.4	--	%	ISO 62
Equilibrium, 23°C, 50% RH	1.4	--	%	ISO 62

Mechanical	Dry	Conditioned	Unit	Test Method
Tensile Modulus (23°C)	10500	6500	MPa	ISO 527-2/1
Tensile Stress (Break, 23°C)	135	85.0	MPa	ISO 527-2/5
Tensile Strain (Break, 23°C)	2.8	5.4	%	ISO 527-2/5
Flexural Modulus ⁵(23°C)	9300	5600	MPa	ISO 178/A
Flexural Stress				ISO 178/A
3.5% strain, 23°C	--	120	MPa	ISO 178/A
23°C ⁶	215	135	MPa	ISO 178/A
Flexural Strain at Flexural Strength ⁷(23°C)	3.1	5.2	%	ISO 178/A

Additional Information	Dry	Conditioned		Test Method
ISO Shortname	PA 66, GFHR, 14-100, GF30,	--		ISO 1874

Injection	Dry	Unit	Test Method
Residual Moisture Content	0.030 - 0.070	%	Karl Fisher

Impact	Dry	Conditioned	Unit	Test Method
Charpy Notched Impact Strength				ISO 179/1eA
-30°C	< 10	--	kJ/m²	ISO 179/1eA
23°C	< 10	--	kJ/m²	ISO 179/1eA
Charpy Unnotched Impact Strength				ISO 179/1eU
-30°C	60	--	kJ/m²	ISO 179/1eU
23°C	65	--	kJ/m²	ISO 179/1eU
Notched Izod Impact				ISO 180/1A
-30°C	< 10	--	kJ/m²	ISO 180/1A
23°C	< 10	--	kJ/m²	ISO 180/1A
Unnotched Izod Impact Strength				ISO 180/1U
-30°C	50	--	kJ/m²	ISO 180/1U
23°C	55	57	kJ/m²	ISO 180/1U

Thermal	Dry	Conditioned	Unit	Test Method
Heat Deflection Temperature
0.45 MPa, not annealed	> 250	--	°C	ISO 75-2/B
1.8 MPa, not annealed	224	--	°C	ISO 75-2/A
Vicat Softening Temperature	240	--	°C	ISO 306/B120
Melting Temperature ⁸	260	--	°C	ISO 11357-3

Electrical	Dry	Conditioned	Unit	Test Method
Surface Resistivity	3.0E+16	4.0E+14	ohms	IEC 60093
Volume Resistivity (23°C)	5.0E+15	5.0E+12	ohms·cm	IEC 60093
Dielectric Strength (23°C, 1.00 mm)	39	35	kV/mm	IEC 60243-1
Relative Permittivity				IEC 60250
23°C, 100 Hz	3.90	8.70		IEC 60250
23°C, 1 MHz	3.70	4.10		IEC 60250
Dissipation Factor				IEC 60250
23°C, 100 Hz	8.0E-3	0.13		IEC 60250
23°C, 1 MHz	0.012	0.070		IEC 60250
Comparative Tracking Index (Solution A)	600	--	V	IEC 60112

Flammability	Dry	Conditioned	Unit	Test Method
Flame Rating				UL 94
0.400 mm	V-0	--		UL 94
1.50 mm	V-0	--		UL 94
3.00 mm	V-0	--		UL 94
Glow Wire Flammability Index				IEC 60695-2-12
0.800 mm	960	--	°C	IEC 60695-2-12
1.50 mm	960	--	°C	IEC 60695-2-12
3.00 mm	960	--	°C	IEC 60695-2-12
Glow Wire Ignition Temperature				IEC 60695-2-13
0.750 mm	725	--	°C	IEC 60695-2-13
1.50 mm	725	--	°C	IEC 60695-2-13
3.00 mm	725	--	°C	IEC 60695-2-13

Injection	Dry	Unit	Test Method
Drying Temperature - Dry Air Dryer	80.0	°C
Drying Time - Dry Air Dryer	2.0 - 6.0	hr
Processing (Melt) Temp	265 - 285	°C
Mold Temperature	80.0 - 100	°C

Note Message
1 .	60x60x2mm, 80°C MT, 600 bar
2 .	60x60x2mm
3 .	60x60x2mm, 80°C MT, 600 bar
4 .	60x60x2mm
5 .	2.0 mm/min
6 .	2.0 mm/min
7 .	2 mm/min
8 .	10°C/min

Resin Grade	Manufacturer	Category	Trademark
RTP 204 FR NH	RTP Company	Nylon 66	RTP
FHR EPS 40-3640	Flint Hills Resources, LP	PS (EPS)	FHR EPS
EPDM 764P	The Dow Chemical Company	EPDM	EPDM
LUVOCOM® 50/CF/10/TF/15/BK 100	Lehmann & Voss & Co.	PC	LUVOCOM®
OTECH TPO OTR7788-Molding	OTECH Corporation	TPE	OTECH TPO