Leona™ 1330G
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Asahi Kasei Chemicals Corporation |
| Trademark: | Leona™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | LO3CIO_Leona-1330G.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Leona™ 1330G is a Polyamide 66 (Nylon 66) product. It is available in Africa & Middle East, Asia Pacific, Europe, or North America. Applications of Leona™ 1330G include automotive, engineering/industrial parts and industrial applications. Characteristics include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.48 | -- | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | Internal Method | |||
| Across Flow | 1.0 | -- | % | |
| Flow | 0.50 | -- | % | |
| Water Absorption | ||||
| Saturation, 23°C | -- | 1.4 | % | |
| Equilibrium, 23°C, 50% RH | -- | 1.4 | % | ISO 62 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness | ASTM D785, ISO 2039-2 | |||
| M-Scale | 89 | 60 | ||
| R-Scale | 120 | 108 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 9800 | 6700 | MPa | ISO 527-2 |
| Tensile Stress | ||||
| Break, 23°C | 144 | 107 | MPa | ISO 527-2 |
| -- | 157 | 118 | MPa | ASTM D638 |
| Tensile Elongation | ||||
| Break | 3.0 | 3.0 | % | ASTM D638 |
| Break, 23°C | 4.0 | 6.0 | % | ISO 527-2 |
| Flexural Modulus | ||||
| -- | 8000 | 6300 | MPa | ASTM D790 |
| 23°C | 8700 | 6000 | MPa | ISO 178 |
| Flexural Strength | ||||
| -- | 245 | 177 | MPa | ASTM D790 |
| 23°C | 235 | 165 | MPa | ISO 178 |
| Taber Abrasion Resistance (1000 Cycles) | -- | 9.00 | mg | ASTM D1044 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | 10 | 13 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength | 71 | 78 | kJ/m² | ISO 179 |
| Notched Izod Impact | 98 | 120 | J/m | ASTM D256 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load | ||||
| 0.45 MPa, Unannealed | 260 | -- | °C | ASTM D648 |
| 0.45 MPa, Unannealed | 261 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 248 | -- | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 246 | -- | °C | ISO 75-2/A |
| CLTE - Flow | 3.0E-5 | -- | cm/cm/°C | ASTM D696 |
| Flammability | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| Flame Rating (0.750 mm) | HB | -- | UL 94 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ultrathene® UE672006 | LyondellBasell Industries | EVA | Ultrathene® |
| Borealis PE FS1470 | Borealis AG | HDPE | Borealis PE |
| KOPLA PA66 KDP1000F | KOPLA Co., Ltd. | Nylon 66 | KOPLA PA66 |
| KOPLA PA6 KNP1000F | KOPLA Co., Ltd. | Nylon 6 | KOPLA PA6 |
| Sylvin 8940-75 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |