Badamid庐 B70 GF30 TM-Z1
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Bada AG |
| Trademark: | Badamid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | LNA8BN_Badamid-B70-GF30-TM-Z1.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Badamid®B70 GF30 TM-Z1 is a polyamide 6 (nylon 6) material, which contains a 30% glass fiber reinforced material. This product is available in Europe,. Badamid®The main characteristics of B70 GF30 TM-Z1 are: flame retardant/rated flame. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Forms |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.35 | -- | g/cm³ | ISO 1183 |
| Water Absorption | ISO 62 | |||
| Saturated, 23°C | 6.3 | -- | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 2.0 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 8800 | 6000 | MPa | ISO 527-2/1 |
| Tensile Stress (Break, 23°C) | 160 | 120 | MPa | ISO 527-2/5 |
| Tensile Strain (Break, 23°C) | 3.5 | 5.5 | % | ISO 527-2/5 |
| Flexural Stress (23°C) | 230 | 200 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 14 | 19 | kJ/m² | ISO 179/1eA |
| 23°C | 16 | 22 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 85 | 95 | kJ/m² | ISO 179/1eU |
| 23°C | 95 | 110 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact | ISO 180/1A | |||
| -30°C | 10 | 16 | kJ/m² | ISO 180/1A |
| 23°C | 15 | 20 | kJ/m² | ISO 180/1A |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature 1 | ||||
| 0.45 MPa, not annealed | 215 | -- | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 200 | -- | °C | ISO 75-2/A |
| Melting Temperature (DSC) | 222 | -- | °C | ISO 3146 |
| Linear thermal expansion coefficient | ISO 11359-2 | |||
| Flow : 4.00mm | 2.3E-5 | -- | cm/cm/°C | ISO 11359-2 |
| Lateral : 4.00mm | 6.3E-5 | -- | cm/cm/°C | ISO 11359-2 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+12 | 1.0E+10 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | 1.0E+12 | ohms·cm | IEC 60093 |
| Dielectric Constant (1 MHz) | 3.70 | 6.70 | IEC 60250 | |
| Dissipation Factor (1 MHz) | 0.023 | 0.21 | IEC 60250 | |
| Comparative Tracking Index | 500 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 0.800 mm | HB | -- | UL 94 | |
| 1.60 mm | HB | -- | UL 94 |
| Additional Information |
|---|
| 干燥 Short-Term Heat Resistance, IEC 216, 20000 hrs: 180°CLong-Term Heat Resistance, IEC 216, 50% decrease of yield stress: 90°C |
| Injection | Dry | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 260 - 280 | °C | |
| Mold Temperature | 80.0 - 90.0 | °C |
| Note Message | |
|---|---|
| 1 . | 110x10x4mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Bergamid™ NN-33GF/000 BLACK | PolyOne Corporation | Nylon 66 | Bergamid™ |
| DELPET™ LP-1 | Asahi Kasei Chemicals Corporation | Acrylic (PMMA) | DELPET™ |
| Karina BLACK PVC COMPOUND 809D48/ 1-C-IS-AS-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Pinnacle PP 5112C3 | Pinnacle Polymers | PP Random Copolymer | Pinnacle PP |
| Sylvin 6034-85 Green 3196 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |