Vydyne® R860 BK02
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Ascend Performance Materials Operations LLC |
| Trademark: | Vydyne® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | LMgEQF_Vydyne-R860-BK02.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Vydyne R860 BK02 is general-purpose, glass-fiber and mineral-reinforced PA66 resin. Available in black, this product is also lubricated for improved flow and offers superior surface appearance. Glass fiber and mineral-reinforced Vydyne resins provide higher heat distortion temperature, resistance to creep and better dimensional stability when compared with unreinforced PA66. These products have good chemical resistance to a broad range of chemicals including gasoline, hydraulic fluids and most solvents. Typical Applications/End Uses: Vydyne R860 BK02 can be successfully used in a wide range of injection-molding engineering applications. Typical parts include automotive clips, radiator shrouds, fans and mirror brackets; electrical connectors, housings and bobbins; and industrial applications such as gears, bearing shells, covers and housings. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| UL File Number |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.47 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow : 23°C, 2.00 mm | 0.80 | -- | % | |
| Flow : 23°C, 2.00 mm | 0.25 | -- | % | |
| Water Absorption | ISO 62 | |||
| 23°C, 24 hr | 0.60 | -- | % | |
| Equilibrium, 23°C, 50% RH | 2.0 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 10000 | 5900 | MPa | ISO 527-2 |
| Tensile Stress (Break, 23°C) | 120 | 90.0 | MPa | ISO 527-2 |
| Tensile Strain (Break, 23°C) | 2.5 | 2.8 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 9000 | 4500 | MPa | ISO 178 |
| Flexural Stress (23°C) | 190 | 97.0 | MPa | ISO 178 |
| Poisson's Ratio | 0.40 | -- | ISO 527-2 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | |||
| -30°C | 3.8 | 6.0 | kJ/m² | |
| 23°C | 4.4 | 10 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179 | |||
| -30°C | 43 | 60 | kJ/m² | |
| 23°C | 48 | 56 | kJ/m² | |
| Notched Izod Impact Strength | ISO 180 | |||
| -30°C | 4.6 | 6.5 | kJ/m² | |
| 23°C | 5.6 | 10 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 230 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 215 | -- | °C | ISO 75-2/A |
| Melting Temperature | 255 | -- | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | |||
| Flow : 23 to 55°C, 2.00 mm | 2.4E-4 | -- | cm/cm/°C | |
| Transverse : 23 to 55°C, 2.00 mm | 6.9E-4 | -- | cm/cm/°C |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Regrind | 25 | % | |
| Rear Temperature | 280 to 310 | °C | |
| Middle Temperature | 280 to 310 | °C | |
| Front Temperature | 280 to 310 | °C | |
| Nozzle Temperature | 280 to 310 | °C | |
| Processing (Melt) Temp | 285 to 305 | °C | |
| Mold Temperature | 65.0 to 95.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Makrolon® 6455 | Covestro - Polycarbonates | PC | Makrolon® |
| Sylvin 8803-85 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Moplen HP462S | LyondellBasell Industries | PP Homopolymer | Moplen |
| Sylvin 9778-75 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Sylvin 9067-80 YELLOW 495 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |