Torelina® A610M-X03
| Category: | PPS , Polyphenylene Sulfide |
| Manufacturer: | Toray Resin Company |
| Trademark: | Torelina® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | LMW3MS_Torelina-A610M-X03.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Torelina® A610M-X03 is a Polyphenylene Sulfide (PPS) product filled with 65% glass\mineral. It is available in Asia Pacific, Europe, or North America. Characteristics include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Part Marking Code |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.97 | g/cm³ | ISO 1183 |
| Molding Shrinkage | Internal Method | ||
| Across Flow : 3.00 mm 1 | 0.60 | % | |
| Flow : 3.00 mm 2 | 0.20 | % | |
| Water Absorption (23°C, 24 hr) | 0.020 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 123 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (23°C) | 140 | MPa | ISO 527-2 |
| Tensile Strain (Break, 23°C) | 1.0 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 21500 | MPa | ISO 178 |
| Flexural Stress (23°C) | 230 | MPa | ISO 178 |
| Shear Strength (23°C) | 65.0 | MPa | JIS K7214 |
| Coefficient of Friction 3 | 0.30 | ||
| Taber Abrasion Resistance (1000 Cycles) | 70.0 | mg | ISO 9352 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 7.0 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 21 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 260 | °C | ISO 75-2/A |
| Melting Temperature | 278 | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | ||
| Flow | 1.8E-5 | cm/cm/°C | |
| Transverse | 2.4E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+16 | ohms·cm | IEC 60093 |
| Electric Strength | 21 | kV/mm | IEC 60243-1 |
| Dielectric Constant 4(23°C, 1 MHz) | 5.10 | IEC 60250 | |
| Dissipation Factor 5(23°C, 1 MHz) | 2.0E-3 | IEC 60250 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.730 mm) | V-0 | UL 94 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Bar Flow Length 6(320°C, 1.00 mm) | 9.00 | cm | Internal Method |
| Note Message | |
|---|---|
| 1 . | 80x80x3 |
| 2 . | 80x80x3mm |
| 3 . | vs. Metal |
| 4 . | 60% RH |
| 5 . | 60% RH |
| 6 . | 98 MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SEQUEL® 1718-UV RXF | LyondellBasell Industries | Polyolefin, Unspecified | SEQUEL® |
| Tenac™-C 7520 | Asahi Kasei Chemicals Corporation | Acetal (POM) Copolymer | Tenac™-C |
| TUFNYL® SFRO BLACK | SRF Ltd. | Nylon 6 | TUFNYL® |
| Iupilon® ELV2010 | Mitsubishi Engineering-Plastics Corp | PC | Iupilon® |
| ALCOM® PWL 10/1 WT1130-09LB | ALBIS PLASTIC GmbH | PC | ALCOM® PWL |