PELPRENE™ P46D-01
| Category: | TPEE , Thermoplastic Polyester Elastomer |
| Manufacturer: | TOYOBO America, Inc. |
| Trademark: | PELPRENE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | LMMPO7_PELPRENE-P46D-01.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PELPRENE™P46D-01 is a thermoplastic polyester elastomer (TPEE) product,. It is available in North America. Features include:
|
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.15 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 0.50 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (2.00 mm) | 0.70 | % | ASTM D955 |
| Water Absorption (Equilibrium, 23°C, 65% RH) | 0.45 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 46 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 31.9 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 700 | % | ASTM D638 |
| Flexural Modulus | 110 | MPa | ASTM D790 |
| Compressive Modulus | 9.60 | MPa | ASTM D695 |
| Taber Abrasion Resistance (1000 Cycles) | 10.0 | mg | ASTM D1044 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tear Strength | 165 | kN/m | ASTM D624 |
| Compression Set | 55 | % | ASTM D395 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | No Break | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 74.0 | °C | ASTM D648 |
| Brittleness Temperature | -65.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 153 | °C | ASTM D1525 |
| Melting Temperature | 203 | °C | DSC |
| CLTE - Flow | 1.7E-4 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 4.0E+13 | ohms·cm | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Additional Information |
|---|
| Hardness, JIS K6301, A scale: 97Resilience, JIS K6301: 70 %Dielectric Strength, JIS K2111: 25 MV/mThe value listed as Compression Set, ASTM D395 was tested according to the JIS K6301 standard.The value listed as Brittle Point, ASTM D746 was tested according to the JIS K6301 standard.Coefficient of Linear Thermal Expansion, TMA: 17e-5 1/KCompression Modulus, ASTM D695, 10%: 9.6 MPaTensile Modulus, ASTM D638, 50% Modulus: 15.2 MPaThe value listed as Brittle Temp ASTM D746, was tested in accordance with JIS K6301. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ravago Compounds PP-4290 | Ravago Manufacturing Americas, LLC | PP Impact Copolymer | Ravago Compounds |
| Tectron H2408 | TECTRON Systems Pte Ltd | TPV | Tectron |
| GLAMIDE® T-402FR | TOYOBO America, Inc. | Nylon 6 | GLAMIDE® |
| Lion Idemitsu Composites PPS K521A2 | Lion Idemitsu Composites Co., Ltd. | PPS | Lion Idemitsu Composites PPS |
| Karina IVORY PVC COMPOUND 802-35/1-IS-RG | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |