GELOY HRA170E is a high heat resistant ASA+PC. It shows high impact retention, which can be positioned for various outdoor and indoor applications requiring superior heat aging properties and colour stability. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.15 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (260°C/5.0 kg) | 17.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow 1 | 0.40 - 0.60 | % | Internal method |
| Water Absorption | ISO 62 | ||
| Saturated, 23°C | 0.60 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.20 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 120 | ISO 2039-2 | |
| Ball Indentation Hardness (H 358/30) | 106 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2500 | MPa | ISO 527-2/1 |
| Tensile Stress | |||
| Yield | 55.0 | MPa | ISO 527-2/5 |
| Yield | 62.0 | MPa | ISO 527-2/50 |
| Fracture | 60.0 | MPa | ISO 527-2/5 |
| Fracture | 62.0 | MPa | ISO 527-2/50 |
| Tensile Strain | |||
| Yield | 5.0 | % | ISO 527-2/5 |
| Yield | 4.0 | % | ISO 527-2/50 |
| Fracture | 130 | % | ISO 527-2/5 |
| Fracture | > 50 | % | ISO 527-2/50 |
| Flexural Modulus 2 | 2400 | MPa | ISO 178 |
| Flexural Stress | 85.0 | MPa | ISO 178 |
| Taber Abrasion Resistance (1000 Cycles, 1000 g, CS-17 Wheel) | 95.0 | mg | Internal method |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 3 | ISO 179/1eA | ||
| -30°C | 12 | kJ/m² | ISO 179/1eA |
| 23°C | 45 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact 4 | ISO 180/1A | ||
| -30°C | 15 | kJ/m² | ISO 180/1A |
| 23°C | 45 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 5 | |||
| 0.45 MPa, unannealed, 100 mm span | 123 | °C | ISO 75-2/Be |
| 1.8 MPa, unannealed, 100 mm span | 114 | °C | ISO 75-2/Ae |
| Vicat Softening Temperature | |||
| -- | 131 | °C | ISO 306/B50 |
| -- | 134 | °C | ISO 306/B120 |
| Ball Pressure Test (125°C) | Pass | IEC 60695-10-2 | |
| CLTE - Flow (23 to 60°C) | 8.0E-5 | cm/cm/°C | ISO 11359-2 |
| Thermal Conductivity | 0.20 | W/m/K | ISO 8302 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+15 | ohms·cm | IEC 60093 |
| Dielectric Strength (3.20 mm, in Oil) | 17 | kV/mm | IEC 60243-1 |
| Relative Permittivity (1 MHz) | 2.80 | IEC 60250 | |
| Dissipation Factor (1 MHz) | 0.013 | IEC 60250 | |
| Comparative Tracking Index | 225 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.6 mm, Testing by SABIC) | HB | UL 94 | |
| Glow Wire Flammability Index (3.2 mm) | 750 | °C | IEC 60695-2-12 |
| Oxygen Index | 22 | % | ISO 4589-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 - 110 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Hopper Temperature | 60 - 80 | °C | |
| Rear Temperature | 230 - 260 | °C | |
| Middle Temperature | 250 - 290 | °C | |
| Front Temperature | 250 - 290 | °C | |
| Nozzle Temperature | 240 - 280 | °C | |
| Processing (Melt) Temp | 260 - 290 | °C | |
| Mold Temperature | 60 - 90 | °C |
| Note Message | |
|---|---|
| 1 . | Tensile Bar |
| 2 . | 2.0 mm/min |
| 3 . | 80*10*4 sp=62mm |
| 4 . | 80*10*4 |
| 5 . | 120*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sanren Y600 (On-spec.) | SINOPEC Shanghai Petrochemical Co. Ltd. | PP Homopolymer | Sanren |
| Extir® GEO 3000 AE | Versalis S.p.A. | PS (EPS) | Extir® |
| Grilamid® LV-30H FWA black 9225 | EMS-GRIVORY | Nylon 12 | Grilamid® |
| Kingfa JH720 G15 | Kingfa | PC Alloy | Kingfa |
| LG PMMA IH830B | LG MMA Corp. | Acrylic (PMMA) | LG PMMA |