LONGLITE® PET 9030-200
| Category: | PET , Polyethylene Terephthalate |
| Manufacturer: | CCP Group |
| Trademark: | LONGLITE® PET |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | LLhMk0_LONGLITE-PET-9030-200.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PET 9030-200 is a 30% glass fiber reinforced injection molding grade. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.54 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (270°C/2.16 kg) | 28 | g/10 min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow | 0.70 to 1.1 | % | |
| Flow | 0.10 to 0.40 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 10000 | MPa | ISO 527-2 |
| Tensile Stress (Break, 23°C) | 135 | MPa | ISO 527-2 |
| Tensile Strain (Break, 23°C) | 2.5 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 8000 | MPa | ISO 178 |
| Flexural Stress (23°C) | 190 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 11 | kJ/m² | ISO 179/1eA |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 240 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 220 | °C | ISO 75-2/A |
| Melting Temperature | 252 | °C | ISO 11357-3 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+13 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+14 | ohms·cm | IEC 60093 |
| Electric Strength (2.00 mm) | 22 | kV/mm | IEC 60243-1 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 to 140 | °C | |
| Drying Time | 4.0 | hr | |
| Processing (Melt) Temp | 265 to 300 | °C | |
| Mold Temperature | 100 to 120 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Stat-Rite® S-1110 | Lubrizol Advanced Materials, Inc. | PE, Unspecified | Stat-Rite® |
| TRIREX® 3022U | Samyang Corporation | PC | TRIREX® |
| Xuchuan XAC-89 | Xuchuan Chemical (Suzhou) Co., Ltd | PUR, Unspecified | Xuchuan |
| Dynalloy™ OBC8000-T60 | PolyOne Corporation | TPE | Dynalloy™ |
| Sylvin 9655-75 Clear 876 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |