PRL PPX-G15
| Category: | PPE+PS , Polyphenylene Ether + PS |
| Manufacturer: | Polymer Resources Ltd. |
| Trademark: | PRL |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | LLeE0y_PRL-PPX-G15.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PRL PPX-G15 is a polyphenylene ether + PS (PPE + PS) product, which contains a 15% glass fiber reinforced material. It can be processed by injection molding and is available in North America. Features include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.17 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (250°C/11.6 kg) | 1.0 - 8.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.18 mm) | 0.20 - 0.50 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (L-Scale) | 105 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield, 3.18mm | 82.7 | MPa | ASTM D638 |
| Fracture, 3.18mm | 82.7 | MPa | ASTM D638 |
| Tensile Elongation (Break, 3.18 mm) | 3.5 | % | ASTM D638 |
| Flexural Modulus (3.18 mm) | 4310 | MPa | ASTM D790 |
| Flexural Strength (3.18 mm) | 121 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 7.4 | kJ/m² | ISO 179/1 |
| Notched Izod Impact | |||
| -30°C, 3.18 mm | 69 | J/m | ASTM D256 |
| 23°C, 3.18 mm | 91 | J/m | ASTM D256 |
| 23°C | 7.4 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, unannealed, 3.18mm | 132 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 3.18mm | 127 | °C | ASTM D648 |
| Vicat Softening Temperature | 141 | °C | ASTM D1525 1 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| Additional Information |
|---|
| Preliminary Data |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 104 - 110 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Rear Temperature | 260 - 304 | °C | |
| Middle Temperature | 271 - 310 | °C | |
| Front Temperature | 282 - 316 | °C | |
| Processing (Melt) Temp | 288 - 316 | °C | |
| Mold Temperature | 71.1 - 104 | °C |
| Note Message | |
|---|---|
| 1 . | 标准 B (120°C/h), 载荷2 (50N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 200 TFE 30 | RTP Company | Nylon 66 | RTP |
| CERTENE™ PBS-07NB | Muehlstein | PP Impact Copolymer | CERTENE™ |
| Ekaloy® 20 E I 6 | Sattler KunststoffWerk GmbH | PC+ABS | Ekaloy® |
| KRATON® D1161 K | Kraton Polymers LLC | SIS | KRATON® |
| Karina RED PVC COMPOUND 835-42/14-IS-RG | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |