LG ABS HT700
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | LG Chem Ltd. |
| Trademark: | LG ABS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | LLAXOq_LG-ABS-HT700.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Description High Stiffness Application Electric&Electronic Products, Miscellaneous Goods |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Multi-Point Data |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.05 | g/cm³ | ASTM D792 |
| -- | 1060 | kg/m³ | ISO 1183 1 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 20 | g/10 min | ASTM D1238 |
| Melt volume-flow rate (220°C/10.0 kg) | 21.2 | cm³/10min | ISO 1133 2 |
| Molding Shrinkage - Flow (3.20 mm) | 0.40 to 0.70 | % | ASTM D955 |
| Water Absorption (Saturation) | 0.31 | % | ISO 62 3 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 113 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| 3.20 mm 4 | 2380 | MPa | ASTM D638 |
| -- | 2500 | MPa | ISO 527-2 5 |
| Tensile Strength | |||
| Yield, 3.20 mm 6 | 53.0 | MPa | ASTM D638 |
| Yield | 50.0 | MPa | ISO 527-2 7 |
| Tensile Strain | |||
| Yield | 6.0 | % | ISO 527-2 8 |
| Break, 3.20 mm 9 | > 10 | % | ASTM D638 |
| Nominal strain at break | 9.0 | % | ISO 527-2 10 |
| Flexural Modulus 11(3.20 mm) | 2790 | MPa | ASTM D790 |
| Flexural Strength 12(3.20 mm) | 86.3 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy notched impact strength | ISO 179/1eA 13 | ||
| -30°C | 6.00 | kJ/m² | |
| 23°C | 15.4 | kJ/m² | |
| Charpy impact strength | ISO 179/1eU 14 | ||
| -30°C | 48.2 | kJ/m² | |
| 23°C | 78.6 | kJ/m² | |
| Notched Izod Impact | ASTM D256 | ||
| -30°C, 3.20 mm | 59 | J/m | |
| -30°C, 6.40 mm | 78 | J/m | |
| 23°C, 3.20 mm | 220 | J/m | |
| 23°C, 6.40 mm | 200 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 6.40 mm | 90.0 | °C | |
| 1.8 MPa, Unannealed, 6.40 mm | 87.0 | °C | |
| Glass Transition Temperature 15 | 100 | °C | ISO 11357-2 16 |
| Vicat Softening Temperature | |||
| -- | 95.0 | °C | ASTM D1525 17 |
| 50°C/h, B (50N) | 95.2 | °C | ISO 306 18 |
| CLTE | ISO 11359-2 19 | ||
| Flow | 8.4E-5 | cm/cm/°C | |
| Transverse | 9.8E-5 | cm/cm/°C | |
| RTI Elec | 60.0 | °C | UL 746 |
| RTI Imp | 60.0 | °C | UL 746 |
| RTI Str | 60.0 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+15 | ohms·cm | ASTM D257 |
| Dielectric Strength | 35 | kV/mm | ASTM D149 |
| Arc Resistance | PLC 5 | ASTM D495 | |
| Comparative Tracking Index (CTI) | PLC 0 | UL 746 | |
| High Amp Arc Ignition (HAI) | UL 746 | ||
| 1.50 mm | PLC 0 | ||
| 3.00 mm | PLC 0 | ||
| High Voltage Arc Tracking Rate (HVTR) | PLC 2 | UL 746 | |
| Hot-wire Ignition (HWI) | UL 746 | ||
| 1.50 mm | PLC 4 | ||
| 3.00 mm | PLC 3 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 | |
| Burning Behav. at thickness h (3.20 mm, UL) | HB | ISO 1210 20 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | > 0.010 | % | |
| Rear Temperature | 180 to 200 | °C | |
| Middle Temperature | 190 to 210 | °C | |
| Front Temperature | 200 to 220 | °C | |
| Nozzle Temperature | 200 to 230 | °C | |
| Processing (Melt) Temp | 210 to 240 | °C | |
| Mold Temperature | 40.0 to 70.0 | °C | |
| Back Pressure | 29.4 to 58.8 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 2 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 3 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 4 . | 1.0 mm/min |
| 5 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 6 . | 50 mm/min |
| 7 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 8 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 9 . | 50 mm/min |
| 10 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 11 . | 15 mm/min |
| 12 . | 15 mm/min |
| 13 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 14 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 15 . | 10 °C/min |
| 16 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 17 . | Rate A (50°C/h), Loading 2 (50 N) |
| 18 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 19 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 20 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ravaflex SBR 1500 | Ravago Group | SBR, Unspecified | Ravaflex |
| BorPEX™ HE2590 | Borealis AG | HDPE, HMW | BorPEX™ |
| Borealis PE FA7224 | Borealis AG | LDPE | Borealis PE |
| Hybrid S551 | Ravago Manufacturing Americas, LLC | PC+ABS | Hybrid |
| Sylvin 3210-80HMW Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |