Epocast 50-A1/9816
| Category: | Epoxy , Epoxy; Epoxide |
| Manufacturer: | Huntsman Advanced Materials |
| Trademark: | Epocast |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | LKlGgn_Epocast-50-A1-9816.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| DESCRIPTION: Epocast ® 50-A1 Resin/Hardener 9816 epoxy laminating system is an unfilled, solvent-free, easy-to-handle material for the manufacture or repair of composite structures as well as for filament winding. Epocast® 50-A1 resin/Hardener 9816 epoxy laminating system is self extinguishing. Epocast ® 50-A1 / Hardener 9816 is qualified to BMS 8-201, Type III, Rev. F. This product is also available in a shorter work life version - Epocast ® 50-A1 resin/Hardener 946 epoxy laminating system. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | ASTM D792 | ||
| -- 1 | 1.05 | g/cm³ | ASTM D792 |
| -- | 1.18 | g/cm³ | ASTM D792 |
| -- 2 | 1.21 | g/cm³ | ASTM D792 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Compressive Modulus | ASTM D695 | ||
| -- 3 | 21.6 | MPa | ASTM D695 |
| -- 4 | 24.3 | MPa | ASTM D695 |
| -- 5 | 28.7 | MPa | ASTM D695 |
| Compressive Strength | ASTM D695 | ||
| -- 6 | 338 | MPa | ASTM D695 |
| -- 7 | 319 | MPa | ASTM D695 |
| -- 8 | 316 | MPa | ASTM D695 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flammability | FAR 25.853(a) | ||
| burn length | mm | FAR 25.853(a) | |
| drip extinguishing time | 0.0 | hr | FAR 25.853(a) |
| self extinguishing time | 0.0 | hr | FAR 25.853(a) |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gel Time - System (25°C) 9 | 1.1 | hr | ASTM D2471 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Cure Time (25°C) | 5.0 | day |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components | |||
| Resin | Mixing ratio by weight: 100 | ||
| Hardening method | Mixing ratio by weight: 14 | ||
| Shelf Life (25°C) | 52 | wk | |
| Thermoset Mix Viscosity | ASTM D2196 | ||
| 25°C | 2400 | cP | ASTM D2196 |
| 25°C 10 | 250 | cP | ASTM D2196 |
| 25°C 11 | 7770 | cP | ASTM D2196 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| CURE SCHEDULE: Five days at 77°F (25°C) or two hours at 170-200°F (77-93°C) after room temperature gel. Handling and machining may be done after 16-24 hours at room temperature. |
| Note Message | |
|---|---|
| 1 . | Hardener |
| 2 . | Resin |
| 3 . | Cure 27 days at 77°F |
| 4 . | Cure 7 days at 77°F |
| 5 . | Cure 1 day at 77°F + 2 hr. at 150°F |
| 6 . | Cure 27 days at 77°F |
| 7 . | Cure 1 day at 77°F + 2 hr. at 150°F |
| 8 . | Cure 7 days at 77°F |
| 9 . | 100 gms |
| 10 . | Hardener |
| 11 . | Resin |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RABALON® FJ6371C | Mitsubishi Chemical Performance Polymers, Inc. | TPE | RABALON® |
| Trademark PE LDVA1925.4F | Trademark Plastics Corporation | LDPE+EVA | Trademark PE |
| Nypol® PA B2 G30 UV BRC0001 NT207 | Petropol Industry and Trade of Polymers LTDA | Nylon 6 | Nypol® PA |
| Edgetek™ ET3200-8001 LG | PolyOne Corporation | PC | Edgetek™ |
| Hanwha Total PE PE30 | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | EVA | Hanwha Total PE |