Luran® S KR2866C
| Category: | ASA+PC , Acrylonitrile Styrene Acrylate + PC |
| Manufacturer: | Styrolution |
| Trademark: | Luran® S |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | LKkU7o_Luran-S-KR2866C.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Luran S KR2866C is a blend of ASA and PC with a reduced content of PC. It is characterized by a medium impact toughness and heat resistance. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.11 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) | ISO 1133 | ||
| 220°C/10.0 kg | 5.00 | cm³/10min | |
| 260°C/5.0 kg | 11.0 | cm³/10min | |
| Molding Shrinkage | 0.50 to 0.90 | % | ISO 294-4 |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 0.90 | % | |
| Equilibrium, 23°C, 50% RH | 0.25 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness | 110 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2600 | MPa | ISO 527-2 |
| Tensile Stress (Yield, 23°C) | 60.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield, 23°C) | 3.4 | % | ISO 527-2 |
| Flexural Stress | 90.0 | MPa | ISO 178 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Elongation - MD (Break) | 15 | % |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -30°C | 9.0 | kJ/m² | |
| 23°C | 35 | kJ/m² | |
| Notched Izod Impact Strength | ISO 180/A | ||
| -30°C | 9.0 | kJ/m² | |
| 23°C | 55 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Annealed | 113 | °C | ISO 75-2/B |
| 1.8 MPa, Annealed | 102 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 110 | °C | ISO 306/B50 |
| CLTE - Flow | 8.0E-5 to 1.0E-4 | cm/cm/°C | ISO 11359-2 |
| Thermal Conductivity | 0.17 | W/m/K | DIN 52612 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+13 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+14 | ohms·cm | IEC 60093 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Processing (Melt) Temp | 260 to 300 | °C | |
| Mold Temperature | 80.0 | °C | |
| Injection Velocity | 200 | mm/sec |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RECLAIR® M 26500 | Reliance Industries Limited | LLDPE | RECLAIR® |
| Sanren F800E (On-spec.) | SINOPEC Shanghai Petrochemical Co. Ltd. | PP Random Copolymer | Sanren |
| Tarnamid® T- 27 CF10 | Grupa Azoty S.A. | Nylon 6 | Tarnamid® |
| Ekalon® 26 E I V | Sattler KunststoffWerk GmbH | PC | Ekalon® |
| HIFOR® LF1021 | Westlake Chemical Corporation | LLDPE | HIFOR® |