TOTAL Polyethylene EVA 1005 VN 4
| Category: | EVA , Ethylene Vinyl Acetate Copolymer |
| Manufacturer: | TOTAL Refining & Chemicals |
| Trademark: | TOTAL Polyethylene |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | LKdn2N_TOTAL-Polyethylene-EVA-1005-VN-4.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
EVA 1005 VN 4 is made by a high pressure tubular process. Grade for flexible films with high transparency and good mechanical properties. Application examples: High strength stretch film, coextrusion, green-house film, stretch hood |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Multi-Point Data |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | |||
| -- | 0.935 | g/cm³ | ISO 1183 |
| -- | 935 | kg/m³ | ISO 1183 1 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.75 | g/10 min | ISO 1133 |
| Melt volume-flow rate (190°C/2.16 kg) | 1.00 | cm³/10min | ISO 1133 2 |
| Vinyl Acetate Content | 14.0 | wt% |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- | 65.0 | MPa | ISO 527-2 |
| -- | 75.0 | MPa | ISO 527-2 3 |
| Tensile Stress (Yield) | 6.00 | MPa | ISO 527-2 4 |
| Tensile Strain (Yield) | 25 | % | ISO 527-2 5 |
| Tensile Elongation at Break | > 50 | % | ISO 527-2 6 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-3 | ||
| MD : Yield, 40 µm, blown film | 6.50 | MPa | ISO 527-3 |
| TD : Yield, 40 µm, blown film | 5.00 | MPa | ISO 527-3 |
| MD : Broken, 40 µm, blown film | 36.0 | MPa | ISO 527-3 |
| TD : Broken, 40 µm, blown film | 35.0 | MPa | ISO 527-3 |
| Tensile Elongation | ISO 527-3 | ||
| MD : Broken, 40 µm, blown film | 320 | % | ISO 527-3 |
| TD : Broken, 40 µm, blown film | 610 | % | ISO 527-3 |
| Dart Drop Impact (40 µm, Blown Film) | 600 | g | ISO 7765-1 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | |||
| -- | 72.0 | °C | ISO 306 |
| 50°C/h, B (50N) | 72.0 | °C | ISO 306 7 |
| Melting Temperature (DSC) | |||
| -- | 91.0 | °C | ISO 3146 |
| -- 8 | 93.0 | °C | ISO 11357-3 9 |
| Additional Information |
|---|
| The value listed as Melting Temperature, ISO 3146, was tested in accordance with ISO 11357.Elmendorf, ISO 6383-2, MD, Blown Film, 40 µm: 18 N/mmElmendorf, ISO 6383-2, TD, Blown Film, 40 µm: 30 N/mmHaze, ISO 14782, Blown Film, 40 µm: 2.5% |
| Extrusion instructions |
|---|
| Advised Temperature Profile: 150 to 180°CPossible Range of Thicknesses: 30 to 300 µ |
| Note Message | |
|---|---|
| 1 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 2 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 3 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 4 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 5 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 6 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 7 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 8 . | 10 °C/min |
| 9 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ASI POLYPROPYLENE 3353-01 | A. Schulman Inc. | PP Impact Copolymer | ASI POLYPROPYLENE |
| DIAMALOY ENGINEERED ALLOYS 808 C2 WW | Network Polymers, Inc. | PC Alloy | DIAMALOY ENGINEERED ALLOYS |
| Kpren 135C | Shandong Xuye New Materials Co., Ltd. | CPE | Kpren |
| Softell TKG 300N C12616 | LyondellBasell Industries | PP Copolymer | Softell |
| apigo bio® PM 260 | API SpA | TPO (POE) | apigo bio® |