OP - PC/PBT 604-I
| Category: | PC+PBT , Polycarbonate + PBT |
| Manufacturer: | Oxford Polymers |
| Trademark: | OP - PC/PBT |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | LK383u_OP---PC-PBT-604-I.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
OP-PC/PBT 604-I is a polycarbonate polybutene terephthalate (PC PBT) material,. This product is available in North America and is processed by injection molding. The main features of OP-PC/PBT 604-I are:
|
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.22 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (285°C/2.16 kg) | 10 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.60 - 0.90 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield | 50.3 | MPa | ASTM D638 |
| Fracture | 51.7 | MPa | ASTM D638 |
| Flexural Modulus | 2070 | MPa | ASTM D790 |
| Flexural Strength | 74.5 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (4°C) | 850 | J/m | ASTM D256 |
| Dart Drop Impact (4°C) | 0.904 | J | ASTM D3029 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 98.9 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 93.3 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.59 mm | HB | UL 94 | |
| 3.18 mm | HB | UL 94 |
| Additional Information |
|---|
| Melt Mass -Flow Rate (MFR), ASTM D1238, 285°C/ 2.16kg: 5 to 15 g/10 min |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 107 - 110 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Rear Temperature | 249 - 271 | °C | |
| Middle Temperature | 254 - 277 | °C | |
| Front Temperature | 260 - 282 | °C | |
| Processing (Melt) Temp | 246 - 274 | °C | |
| Mold Temperature | 65.6 - 87.8 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Rilsamid® AZM 30 O TLD | Arkema | Nylon 12 | Rilsamid® |
| Clariant Nylon 6/6 66M40-L | Clariant Corporation | Nylon 66 | Clariant Nylon 6/6 |
| ISOTHANE® 3080A-FR | Great Eastern Resins Industrial Co., Ltd. (GRECO) | TPU-Polyether | ISOTHANE® |
| LNP™ THERMOCOMP™ LF008 compound | SABIC Innovative Plastics | PEEK | LNP™ THERMOCOMP™ |
| Braskem PE SGF4950 | Braskem | HDPE | Braskem PE |