RTP 207 UV
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | LK0MEY_RTP-207-UV.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Glass Fiber - UV Stabilized |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.46 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.20 mm) | 0.10 - 0.40 | % | ASTM D955 |
| Moisture Content | 0.20 | % |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Primary Additive | 40 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 13100 | MPa | ASTM D638 |
| Tensile Strength | 186 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | 2.5 - 3.5 | % | ASTM D638 |
| Flexural Modulus | 11600 | MPa | ASTM D790 |
| Flexural Strength | 296 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm) | 120 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.20 mm) | 1100 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 249 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm, ** Values per RTP Company testing.) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 79.4 | °C | |
| Drying Time | 4.0 | hr | |
| Dew Point | -17.8 | °C | |
| Processing (Melt) Temp | 277 - 299 | °C | |
| Mold Temperature | 65.6 - 107 | °C | |
| Injection Pressure | 68.9 - 124 | MPa |
| Injection instructions |
|---|
| Desiccant Type Dryer Required. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 282 | RTP Company | Nylon 66 | RTP |
| Wellamid® 22LHI4 XE-N | Wellman Engineering Resins | Nylon 66 | Wellamid® |
| KOPLA PC KBP1000 | KOPLA Co., Ltd. | PBT | KOPLA PC |
| Karina CLEAR PVC COMPOUND 80/315-IS-RG | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LEXAN™ EXL9330S resin | SABIC Innovative Plastics Europe | PC | LEXAN™ |