Order Products : sales@su-jiao.com
WPP PP PPH5TF2-Black
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Washington Penn Plastic Co. Inc. |
| Trademark: | WPP PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | LI68Gk_WPP-PP-PPH5TF2-Black.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| WPP PP PPH5TF2-Black is a polypropylene homopolymer (PP Homopoly) product, which contains 20% talc filler. It is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific. Typical application areas are: automotive industry. The main characteristics are: heat stabilizer. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.05 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 16 | g/10 min | ASTM D1238, ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 101 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | |||
| Yield | 33.0 | MPa | ISO 527-2/5 |
| Fracture 1 | 33.0 | MPa | ASTM D638 |
| Tensile Elongation | |||
| Fracture 2 | 28 | % | ASTM D638 |
| Fracture | 37 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| -- 3 | 2600 | MPa | ASTM D790 |
| -- 4 | 2800 | MPa | ISO 178 |
| Flexural Stress | |||
| -- 5 | 54.0 | MPa | ISO 178 |
| Yield 6 | 54.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 34 | J/m | ASTM D256 |
| 23°C | 3.0 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, not annealed | 73.0 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 74.0 | °C | ISO 75-2/A |
| Additional Information |
|---|
| Tested at 23 ± 2°C (73.4 ± 3.6°F) and 50 ± 5% relative humidity unless otherwise noted. |
| Note Message | |
|---|---|
| 1 . | 10 mm/min |
| 2 . | 10 mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 2.0 mm/min |
| 5 . | 2.0 mm/min |
| 6 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PRL PPX-GP7 | Polymer Resources Ltd. | PPE+PS | PRL |
| Desmovit® DP R Eco NF15 | geba Kunststoffcompounds GmbH | TPU-Ester/Ether | Desmovit® |
| Embrace™ HY1000 Compound | Eastman Chemical Company | Copolyester | Embrace™ |
| Karina BROWN PVC COMPOUND 800-36/266-A-ERYB | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LUVOCOM® 1-1108 VP | Lehmann & Voss & Co. | Nylon 66 | LUVOCOM® |