REPRO PP RG6
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Rondo Plast AB |
| Trademark: | REPRO |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | LFzgsH_REPRO-PP-RG6.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PP 30% glassfibre reinforced |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Recycled Content |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.12 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 6.0 | g/10 min | ISO 1133 |
| Molding Shrinkage | ISO 2577 | ||
| Across Flow | 0.50 to 0.70 | % | |
| Flow | 0.25 to 0.35 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Modulus (23°C) | 5000 | MPa | ISO 178 |
| Flexural Stress | 100 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 5.0 | kJ/m² | ISO 179 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 | |
| Glow Wire Ignition Temperature (2.00 mm) | 750 | °C | IEC 60695-2-13 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Processing (Melt) Temp | 205 to 260 | °C | |
| Mold Temperature | 40.0 to 80.0 | °C | |
| Injection Pressure | 40.0 to 110 | MPa | |
| Injection Rate | Fast | ||
| Back Pressure | 1.00 to 2.00 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Niuk 20GP17 | Shanghai Niuk New Plastic Technology Co., Ltd. | ABS | Niuk |
| Durethan® BKV 35 H2.0 901510 | LANXESS Corporation | Nylon 6 | Durethan® |
| HANWHA LLDPE 3121UV | Hanwha Chemical | LLDPE | HANWHA LLDPE |
| Hifax TYC 337P 4 C13098 | LyondellBasell Industries | PP Copolymer | Hifax |
| LNP™ THERMOCOMP™ DX06409 compound | SABIC Innovative Plastics | PC | LNP™ THERMOCOMP™ |