LNP™ THERMOCOMP™ 9X11427 compound
| Category: | TP, Unspecified , Thermoplastic |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | LFz9KA_LNP-THERMOCOMP-9X11427-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP 9X11427 is a compound based on Miscellanbeous resin containing 40% specialty glass filled TP alloy. Added features of this grade include: Ultra-Stiff Toughness, Improved Impact, Good Flow for Thin Wall molding. Also known as: LNP* THERMOCOMP* Compound 9X11427 Product reorder name: 9X11427 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | ASTM D792 | ||
| -- | 1.57 | g/cm³ | |
| -- | 1.56 | g/cm³ | |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 0.20 to 0.40 | % | |
| Across Flow : 24 hr | 0.70 to 0.90 | % | |
| Water Absorption (24 hr, 50% RH) | 0.070 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 14600 | MPa | ASTM D638 |
| -- | 14300 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break 2 | 150 | MPa | ASTM D638 |
| Break | 141 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Break 3 | 2.7 | % | ASTM D638 |
| Break | 2.5 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 4 | 12900 | MPa | ASTM D790 |
| -- 5 | 12300 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 219 | MPa | ISO 178 |
| Yield, 50.0 mm Span 6 | 229 | MPa | ASTM D790 |
| Break, 50.0 mm Span 7 | 227 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 160 | J/m | ASTM D256 |
| 23°C 8 | 12 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 1100 | J/m | ASTM D4812 |
| 23°C 9 | 70 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact (23°C, Total Energy) | 11.0 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 220 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 10 | 218 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 201 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 11 | 198 | °C | ISO 75-2/Af |
| CLTE | ASTM D696 | ||
| Flow : -30 to 30°C | 3.5E-5 | cm/cm/°C | |
| Transverse : -30 to 30°C | 6.8E-5 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.050 | % | |
| Rear Temperature | 221 to 232 | °C | |
| Middle Temperature | 243 to 254 | °C | |
| Front Temperature | 260 to 271 | °C | |
| Processing (Melt) Temp | 238 to 266 | °C | |
| Mold Temperature | 82.2 to 98.9 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 2.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 1.3 mm/min |
| 8 . | 80*10*4 |
| 9 . | 80*10*4 |
| 10 . | 80*10*4 mm |
| 11 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 2800-55A | RTP Company | TPO (POE) | RTP |
| RTP 2800-50D | RTP Company | TPO (POE) | RTP |
| Elastron® G G500.A40.B.PA | Elastron USA, Inc. | SEBS | Elastron® G |
| OXNILON 66 30GF-V0 | Oxford Polymers | Nylon 66 | OXNILON 66 |
| Plaslube® PA6 ML2 HS BK | Techmer Engineered Solutions | Nylon 6 | Plaslube® |