Taitalac® 5000
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Taita Chemical Company, Ltd. |
| Trademark: | Taitalac® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | LF6cn1_Taitalac-5000.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Taitalac®5000 is an acrylonitrile butadiene styrene (ABS) material,. This product is available in North America or Asia Pacific region. The processing method is injection molding. Taitalac®The main features of the 5000 are:
Typical application areas include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| UL File Number |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.04 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 200°C/5.0 kg | 2.0 | g/10 min | ASTM D1238 |
| 220°C/10.0 kg | 20 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | < 0.40 | % | ASTM D955 |
| Water Absorption (24 hr) | < 0.30 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale, 23°C) | 115 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | ASTM D638 | ||
| Yield, 23°C, 3.18mm | 42.1 | MPa | ASTM D638 |
| Fracture, 23°C, 3.18mm | 35.2 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 23°C, 3.18 mm) | 30 | % | ASTM D638 |
| Flexural Modulus 3(23°C) | 2550 | MPa | ASTM D790 |
| Flexural Strength 4(Yield, 23°C) | 73.5 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| 23°C, 3.18 mm | 200 | J/m | ASTM D256 |
| 23°C, 6.35 mm | 180 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 12.7 mm) | 83.0 | °C | ASTM D648 |
| Vicat Softening Temperature | 103 | °C | ASTM D1525 5 |
| RTI Elec (1.57 mm) | 60.0 | °C | UL 746 |
| RTI Imp (1.57 mm) | 60.0 | °C | UL 746 |
| RTI (1.57 mm) | 60.0 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| High Amp Arc Ignition (HAI) (1.57 mm) | 200 | UL 746 | |
| High Voltage Arc Tracking Rate (HVTR) (1.57 mm) | 0.00 | mm/min | UL 746 |
| Hot-wire Ignition (HWI) (1.57 mm) | 18 | sec | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.59 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 - 85.0 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Rear Temperature | 185 - 215 | °C | |
| Middle Temperature | 195 - 225 | °C | |
| Front Temperature | 185 - 215 | °C | |
| Nozzle Temperature | 205 - 235 | °C | |
| Processing (Melt) Temp | 170 - 180 | °C | |
| Mold Temperature | 40.0 - 70.0 | °C | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 0.345 - 0.483 | MPa | |
| Screw Speed | 30 - 100 | rpm |
| Injection instructions |
|---|
| Injection Pressure: Moderate to Moderately High |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 2.8 mm/min |
| 4 . | 2.8 mm/min |
| 5 . | 压 力1 (10N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sinvicomp SFW6500S | Teknor Apex Asia Pacific PTE. LTD. | PVC, Flexible | Sinvicomp |
| TAROMID A 280 Z1 G6 | Taro Plast S.p.A. | Nylon 66 | TAROMID A |
| FHR EPS 55-7655 | Flint Hills Resources, LP | PS (EPS) | FHR EPS |
| POLIMAXX 1126NK | IRPC Public Company Limited | PP Homopolymer | POLIMAXX |
| Sylvin 8915-72 WHITE 1217-1 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |