Fusabond® N 525
| Category: | Ethylene Copolymer , Ethylene Copolymer |
| Manufacturer: | DuPont Packaging & Industrial Polymers |
| Trademark: | Fusabond® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | LElQYp_Fusabond-N-525.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
DuPont™ Fusabond® N525 is an anhydride modified ethylene copolymer. DuPont™ Fusabond® N525 can only be used in the following applications: (1) polyamide (nylon) blends (2) blends for golf ball components (3) blends for "compatibilizing flame retardant fillers in non-halogen flame retardant polyolefin-based wire and cable compounds" |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.880 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 3.7 | g/10 min | ASTM D1238, ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 30 | ASTM D2240, ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Break, 20°C 1 | 14.4 | MPa | ASTM D638 |
| Break, 23°C 2 | 6.43 | MPa | ASTM D638 |
| Break, 20°C 3 | 14.4 | MPa | ISO 527-2/50 |
| Break, 23°C 4 | 6.43 | MPa | ISO 527-2/500 |
| Tensile Elongation | |||
| Break, 23°C 5 | 590 | % | ASTM D638 |
| Break, 23°C 6 | 550 | % | ASTM D638 |
| Break, 23°C 7 | 590 | % | ISO 527-2/50 |
| Break, 23°C 8 | 550 | % | ISO 527-2/500 |
| Flexural Modulus 9(23°C) | 22.5 | MPa | ASTM D790 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Transition Temperature | -48.0 | °C | ASTM D3418 |
| Vicat Softening Temperature | 42.0 | °C | ASTM D1525, ISO 306 |
| Peak Melting Temperature | |||
| -- | 53.9 | °C | ASTM D3418 |
| -- | 54.0 | °C | ISO 3146 |
| Peak Crystallization Temperature (DSC) | 35.0 | °C | ASTM D3418 |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Maximum Processing Temperature | 290 | °C |
| Note Message | |
|---|---|
| 1 . | Type IV, 50 mm/min |
| 2 . | Type IV, 500 mm/min |
| 3 . | Type IV |
| 4 . | Type IV |
| 5 . | Type IV, 50 mm/min |
| 6 . | Type IV, 500 mm/min |
| 7 . | Type IV |
| 8 . | Type IV |
| 9 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ad-Tech Epoxy EL-301-LP | Ad-Tech Plastic Systems Corp. | Epoxy | Ad-Tech Epoxy |
| Hytrel® HTR8685 BK022A | DuPont Performance Polymers | TPC-ET | Hytrel® |
| Karina PINK COLOR CONCENTRATE 39/ 63-FC-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| POLYfill PPC GF2007 PD1 | Polykemi AB | PP Copolymer | POLYfill |
| Sumiliteresin® PR-51350B | SBHPP | Phenolic | Sumiliteresin® |