ACRYLITE® Satinice ZD 24

Category:	Acrylic (PMMA) , Polymethyl Methacrylate Acrylic
Manufacturer:	Evonik Cyro LLC
Trademark:	ACRYLITE®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	LEk2Rp_ACRYLITE-Satinice-ZD-24.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

ACRYLITE® Satinice ZD 24 polymer is an amorphous, impact-modified light diffusing thermoplastic molding and extrusion compound based on polymethyl methacrylate (PMMA).

Typical properties of ACRYLITE® Satinice zd polymers are:

high weather resistance

superior light diffusion (hiding power) and transmittance

improved resistance to stress cracking

good melt flow rate

easy to color

The special properties of ACRYLITE® Satinice ZD 24 polymer are:

high impact/break resistance and strength

high melt strength

high heat resistance

Application:
Used for extrusion applications including profiles and sheet.

General Information
Additive	Impact Modifier
Features	Amorphous Good Colorability Good Flow Good Melt Strength Good Weather Resistance High Heat Resistance High Impact Resistance High Strength Impact Modified
Uses	Automotive Interior Parts Lighting Diffusers Lighting Fixtures Profiles Sheet
Agency Ratings	EC 1907/2006 (REACH)
Forms	Pellets
Processing Method	Extrusion Injection Molding Profile Extrusion Sheet Extrusion

Physical	Nominal Value	Unit	Test Method
Specific Gravity	1.15	g/cm³	ASTM D792
Melt Mass-Flow Rate (MFR) (230°C/3.8 kg)	0.80	g/10 min	ASTM D1238
Molding Shrinkage - Flow	0.30 to 0.60	%	ASTM D955
Water Absorption (Equilibrium)	< 0.30	%	ASTM D570

Hardness	Nominal Value	Unit	Test Method
Rockwell Hardness (M-Scale)	63		ASTM D785

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	2280	MPa	ASTM D638
Tensile Strength	50.5	MPa	ASTM D638
Tensile Elongation			ASTM D638
Yield	4.0 to 6.0	%
Break	43	%
Flexural Modulus	2070	MPa	ASTM D790
Flexural Strength	129	MPa	ASTM D790

Impact	Nominal Value	Unit	Test Method
Notched Izod Impact (23°C, 6.35 mm)	33	J/m	ASTM D256

Thermal	Nominal Value	Unit	Test Method
Deflection Temperature Under Load (1.8 MPa, Annealed, 6.35 mm)	83.3	°C	ASTM D648
Vicat Softening Temperature	97.8	°C	ASTM D1525
CLTE - Flow (0 to 100°C)	7.2E-5	cm/cm/°C	ASTM D696

Flammability	Nominal Value		Test Method
Flame Rating (1.60 mm)	HB		UL 94

Optical	Nominal Value	Unit	Test Method
Refractive Index	1.490		ASTM D542
Transmittance (3200 µm)	87.0	%	ASTM D1003
Haze (3200 µm)	97	%	ASTM D1003
Yellowness Index (3.20 mm)	3.0	YI	ASTM D1925

Resin Grade	Manufacturer	Category	Trademark
Monprene® IN-22058 XRD (PRELIMINARY DATA)	Teknor Apex Company	TPE	Monprene®
Yuyao PA 03ML20	Yuyao Tenglong Plastics Co., Ltd.	Nylon 66/6	Yuyao PA
ExxonMobil™ PP1055E2	ExxonMobil Chemical	PP Homopolymer	ExxonMobil™
DIC.PPS FZ-3600-D5	DIC Corporation	PPS	DIC.PPS
HIFOR® LT74104	Westlake Chemical Corporation	LLDPE	HIFOR®