Quadrant EPP ERTACETAL® H
| Category: | Acetal (POM) Homopolymer , Acetal (POM) Homopolymer |
| Manufacturer: | Quadrant Engineering Plastic Products |
| Trademark: | Quadrant EPP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | LD1dpB_Quadrant-EPP-ERTACETAL-H.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Quadrant EPP ERTACETAL® H is an Acetal (POM) Homopolymer product. It is available in Europe. Characteristics include:
|
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.43 | g/cm³ | ISO 1183 |
| Water Absorption | ISO 62 | ||
| 23°C, 24 hr, 3.00 mm | 0.21 | % | |
| Saturation, 23°C | 0.85 | % | |
| Equilibrium, 23°C, 50% RH | 0.20 | % | |
| Water Absorption | ISO 62 | ||
| 23°C, 3.00 mm 1 | 18.0 | mg | |
| 23°C, 3.00 mm 2 | 0.43 | % | |
| 23°C, 3.00 mm 3 | 36.0 | mg |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Service Temperature - Minimum | -50 | °C |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale, 10.0 mm) | 88 | ISO 2039-2 | |
| Ball Indentation Hardness (10.0 mm) | 160 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 4 | 3600 | MPa | ISO 527-2/1B/1 |
| Tensile Stress 5(Yield) | 78.0 | MPa | ISO 527-2/1B/20 |
| Tensile Strain 6(Break) | 35 | % | ISO 527-2/1B/20 |
| Tensile Creep Modulus (1000 hr) | 15.0 | MPa | ISO 899-1 |
| Compressive Stress | ISO 604/1 | ||
| 5% Strain | 75.0 | MPa | |
| 2% Strain | 40.0 | MPa | |
| 1% Strain | 22.0 | MPa |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 10 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | > 200 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact Strength 7 | 10 | kJ/m² | ISO 180/2A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 115 | °C | ISO 75-2/A |
| Continuous Use Temperature | |||
| -- 8 | 90.0 | °C | |
| -- 9 | 105 | °C | |
| -- 10 | 150 | °C | |
| Melting Temperature (DSC) | 175 | °C | |
| CLTE - Flow | |||
| 23 to 60°C | 9.5E-5 | cm/cm/°C | |
| 23 to 150°C | 1.1E-4 | cm/cm/°C | |
| Thermal Conductivity (23°C) | 0.31 | W/m/K |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity 11 | > 1.0E+13 | ohms | IEC 60093 |
| Volume Resistivity 12 | > 1.0E+14 | ohms·cm | IEC 60093 |
| Electric Strength 13(1.00 mm, in Oil) | 20 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | ||
| 100 Hz 14 | 3.80 | ||
| 1 MHz 15 | 3.80 | ||
| Dissipation Factor | IEC 60250 | ||
| 100 Hz 16 | 3.0E-3 | ||
| 1 MHz 17 | 8.0E-3 | ||
| Comparative Tracking Index 18 | 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 3.00 mm | HB | ||
| 6.00 mm | HB | ||
| Oxygen Index | 15 | % | ISO 4589-2 |
| Note Message | |
|---|---|
| 1 . | Weight, 24 hrs |
| 2 . | 96 hrs |
| 3 . | Weight, 96 hrs |
| 4 . | Conditioned |
| 5 . | Conditioned |
| 6 . | Conditioned |
| 7 . | Conditioned |
| 8 . | 20000 hrs |
| 9 . | 5000 hrs |
| 10 . | Short periods |
| 11 . | Conditioned |
| 12 . | Conditioned |
| 13 . | Conditioned |
| 14 . | Conditioned |
| 15 . | Dry |
| 16 . | Dry |
| 17 . | Conditioned |
| 18 . | Conditioned |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Matrixx FPP1A30CC | The Matrixx Group, Inc. | PP, Unspecified | Matrixx |
| TECHNO ABS R5601A | Techno Polymer America, Inc. | PC+ABS | TECHNO ABS |
| Di-Pak™ E-4595-3 | Hapco Inc. | TP, Unspecified | Di-Pak™ |
| ELASTOSIL® R plus 4306/70 | Wacker Chemie AG | Silicone | ELASTOSIL® R plus |
| Karina NATURAL PVC COMPOUND 701D25/ 1-A-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |