REPOL® H110FG
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Reliance Industries Limited |
| Trademark: | REPOL® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | LBz4Fa_REPOL-H110FG.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| REPOL Polypropylene H110FG is manufactured using Unipol PP process which combines the production efficiency of gas phase fluidized bed reactor technology with the high activity stereospecific catalyst system. Repol H110FG is recommended for use in Fiber Spinning operations, for making multifilament FDY yarns and staple fibres. Repol H110FG is tested for contents from the point of suitability to fibre spinning. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 11 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield) | 35.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Yield) | 10 | % | ASTM D638 |
| Flexural Modulus - 1% Secant 3 | 1450 | MPa | ASTM D790A |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 27 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 104 | °C | ASTM D648 |
| Melting Temperature | 163 | °C | DSC |
| Note Message | |
|---|---|
| 1 . | Type I, 50 mm/min |
| 2 . | Type I, 50 mm/min |
| 3 . | Type I |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Unichem 6507 | Colorite Polymers | PVC, Unspecified | Unichem |
| Xuchuan 6160/B-8260 (Sole) | Xuchuan Chemical (Suzhou) Co., Ltd | PUR, Unspecified | Xuchuan |
| Alpha PVC GW 2326-A-VW1 NAT LCF | AlphaGary | PVC, Unspecified | Alpha PVC |
| EXCELINK 1200B | JSR Corporation | TPV | EXCELINK |
| LNP™ STAT-KON™ MD000AP compound | SABIC Innovative Plastics | PP, Unspecified | LNP™ STAT-KON™ |