Zytel® 101 NC010
| Category: | Nylon 66 , NYLON RESIN |
| Manufacturer: | DuPont Performance Polymers |
| Trademark: | Zytel® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | LBDEyK_Zytel-101-NC010.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Unreinforced Polyamide 66 |
| General Information | |
|---|---|
| Forms |
|
| Processing Method |
|
| Part Marking Code (ISO 11469) |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.14 | -- | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (275°C/1.2 kg) | 24.0 | -- | cm³/10min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 1.4 | -- | % | |
| Flow | 1.4 | -- | % | |
| Water Absorption | ISO 62 | |||
| 23°C, 24 hr, 2.00 mm | 8.5 | -- | % | |
| Equilibrium, 23°C, 2.00 mm, 50% RH | 2.6 | -- | % | |
| Viscosity Number | 145 | -- | cm³/g | ISO 307 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Ball Indentation Hardness | ISO 2039-1 | |||
| H 358/30 | 180 | 85.0 | MPa | |
| H 961/30 | 160 | -- | MPa |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 3100 | 1400 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 82.0 | 55.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield) | 4.5 | 25 | % | ISO 527-2 |
| Nominal Tensile Strain at Break | 25 | > 50 | % | ISO 527-2 |
| Tensile Creep Modulus | ISO 899-1 | |||
| 1 hr | -- | 1200 | MPa | |
| 1000 hr | -- | 700 | MPa | |
| Flexural Modulus | 2800 | 1200 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 4.5 | 3.0 | kJ/m² | |
| 23°C | 5.5 | 15 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 400 kJ/m² | No Break | ||
| 23°C | No Break | No Break | ||
| Notched Izod Impact Strength | ISO 180/1A | |||
| -40°C | 5.5 | -- | kJ/m² | |
| -30°C | 5.5 | -- | kJ/m² | |
| 23°C | 5.5 | 12 | kJ/m² | |
| Unnotched Izod Impact Strength | ISO 180/1U | |||
| -30°C | 300 | -- | kJ/m² | |
| 23°C | No Break | No Break |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 200 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 70.0 | -- | °C | ISO 75-2/A |
| Glass Transition Temperature 1 | 60.0 | -- | °C | ISO 11357-2 |
| Vicat Softening Temperature | 240 | -- | °C | ISO 306/B50 |
| Melting Temperature 2 | 262 | -- | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | |||
| Flow | 1.0E-4 | -- | cm/cm/°C | |
| Transverse | 1.1E-4 | -- | cm/cm/°C |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | -- | 1.0E+12 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | 1.0E+13 | ohms·cm | IEC 60093 |
| Electric Strength | 32 | 28 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | |||
| 100 Hz | 3.80 | 6.00 | ||
| 1 MHz | 3.50 | 4.00 | ||
| Dissipation Factor | IEC 60250 | |||
| 100 Hz | 8.0E-3 | 0.21 | ||
| 1 MHz | 0.018 | 0.075 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flammability Classification | IEC 60695-11-10, -20 | |||
| 0.710 mm | V-2 | -- | ||
| 1.50 mm | V-2 | -- | ||
| Oxygen Index | 28 | -- | % | ISO 4589-2 |
| Fill Analysis | Dry | Conditioned | Unit | |
|---|---|---|---|---|
| Melt Density | 0.980 | -- | g/cm³ | |
| Specific Heat Capacity of Melt | 2790 | -- | J/kg/°C | |
| Thermal Conductivity of Melt | 0.16 | -- | W/m/K |
| Additional Information | Dry | Conditioned | Unit | |
|---|---|---|---|---|
| Effective Thermal Diffusivity | 0.0500 | -- | cSt |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| 2 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tenac™-C 4520 | Asahi Kasei Chemicals Corporation | Acetal (POM) Copolymer | Tenac™-C |
| Elastollan® B 90 A | BASF Polyurethanes GmbH | TPU-Polyester | Elastollan® |
| Elastron® G G500.A80.B.ABS | Elastron USA, Inc. | SEBS | Elastron® G |
| LEXAN™ HPH4504H resin | SABIC Innovative Plastics | PPC | LEXAN™ |
| PEARLSTICK® 46-10/16 | Lubrizol Advanced Materials, Inc. | TPU-Polyester | PEARLSTICK® |