Order Products : sales@su-jiao.com
WELLAMID Nylon 6600 CFGV 20/10 HWCP
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | CP-Polymer-Technik GmbH & Co. KG |
| Trademark: | WELLAMID Nylon |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | LAktvX_WELLAMIDNylon6600CFGV2010HWCP.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
WELLAMID Nylon 6600 CFGV 20/10 HWCP is a polyamide 66 (nylon 66) material, which contains 10% glass fiber reinforcement and 20% carbon fiber reinforcement. This product is available in Europe,. The main features of WELLAMID Nylon 6600 CFGV 20/10 HWCP are:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.35 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ||||
| Transverse flow : 4.00mm | 0.70 | -- | % | |
| Flow : 4.00mm | 0.20 | -- | % | |
| Water Absorption (Saturation, 23°C) | 1.8 - 2.3 | -- | % | DIN 53495 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 16500 | 13000 | MPa | ISO 527-2 |
| Tensile Stress | 200 | 135 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 2.0 | 4.0 | % | ISO 527-2/5 |
| Flexural Modulus | 14000 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 9.0 | 22 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 50 | 85 | kJ/m² | ISO 179 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, not annealed | 250 | -- | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 250 | -- | °C | ISO 75-2/A |
| Vicat Softening Temperature | 230 | -- | °C | ISO 306/B50 |
| Melting Temperature | 255 | -- | °C | |
| CLTE - Flow (23 to 80°C) | 2.5E-5 | -- | cm/cm/°C | DIN 53752 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | < 20 | -- | ohms | IEC 60093 |
| Volume Resistivity | < 10 | -- | ohms·cm | IEC 60093 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 1.6 mm | HB | HB | UL 94 | |
| 3.2 mm | HB | HB | UL 94 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 275 - 295 | °C | |
| Mold Temperature | 80 - 100 | °C | |
| Injection Rate | Fast |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shinko-Lac® ASA S310 | Mitsubishi Rayon America Inc. | ASA | Shinko-Lac® |
| ULTEM™ CRS5301 resin | SABIC Innovative Plastics | PEI | ULTEM™ |
| Hapcast™ 3731 | Hapco Inc. | TP, Unspecified | Hapcast™ |
| K-vinyl 105 Deg C Rating Insulation (85-Dry) | Technovinyl Polymers India Ltd. | PVC, Unspecified | K-vinyl |
| PLUSTEK PA313G43 | Polyram Ram-On Industries | Nylon 66 | PLUSTEK |