ENGAGE™ 8003

Category:	TPO (POE) , Polyolefin Elastomer
Manufacturer:	The Dow Chemical Company
Trademark:	ENGAGE™
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	LAkd9v_ENGAGE-8003.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

ENGAGE™ 8003 Polyolefin Elastomer is an ethylene-octene copolymer that has excellent flow characteristics and performs well in a wide variety of general purpose thermoplastic elastomer applications.

ENGAGE 8003 provides superb impact properties in blends with polypropylene (PP) and polyethylene (PE). It also provides high filler loading capability and outstanding peroxide cure capability. When cross-linked by peroxide, silane, or irradiation, it gives exceptional heat aging, compression set, and weather resistance properties, and may be used to produce high performance electrical insulation and jacketing.

Main Characteristics:

Pellet form

Excellent flow characteristics

Improved impact in polypropylene and polyethylene

High filler loading

Peroxide, silane, and radiation curable

Exceptional heat aging, compression set, and weather resistance

Complies with:

U.S. FDA 21 CFR 177.1520(c)3.2c

EU, No 10/2011

Japan Hygienic Olefin and Styrene Plastics Association

U.S. FDA DMF

Consult the regulations for complete details.

Applications:

General purpose thermoplastic elastomers

Wire and cable

Impact modification

General Information
Agency Ratings	DMF Unspecified Rating EU No 10/2011 FDA 21 CFR 177.1520(c) 3.2c JHOSPA Unspecified Rating
Forms	Pellets

Physical	Nominal Value	Unit	Test Method
Specific Gravity	0.885	g/cm³	ASTM D792
Melt Mass-Flow Rate (MFR) (190°C/2.16 kg)	1.0	g/10 min	ASTM D1238
Mooney Viscosity (ML 1+4, 121°C)	22	MU	ASTM D1646

Hardness	Nominal Value	Unit	Test Method
Durometer Hardness			ASTM D2240
Shore A, Compression Molded	84
Shore D, Compression Molded	31

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus - 100% Secant ¹(Compression Molded)	4.80	MPa	ASTM D638
Tensile Strength ²(Break, Compression Molded)	18.2	MPa	ASTM D638
Tensile Elongation ³(Break, Compression Molded)	640	%	ASTM D638
Flexural Modulus			ASTM D790
1% Secant : Compression Molded	33.7	MPa
2% Secant : Compression Molded	32.6	MPa

Elastomers	Nominal Value	Unit	Test Method
Tear Strength ⁴	61.0	kN/m	ASTM D624

Thermal	Nominal Value	Unit	Test Method
Glass Transition Temperature	-46.0	°C	Internal Method
Vicat Softening Temperature	63.0	°C	ASTM D1525
Melting Temperature (DSC) ⁵	77.0	°C	Internal Method
Peak Crystallization Temperature (DSC)	60.0	°C	Internal Method

Note Message
1 .	510 mm/min
2 .	510 mm/min
3 .	510 mm/min
4 .	Die C
5 .	10°C/min

Resin Grade	Manufacturer	Category	Trademark
Shandong Nylon A4TR05	Shandong Dongchen Engineering Plastics Co., Ltd.	Nylon, Unspecified	Shandong Nylon
Starex SD-0150 U	SAMSUNG SDI CO., LTD.	ABS	Starex
Stat-Rite® S-1110	Lubrizol Advanced Materials, Inc.	PE, Unspecified	Stat-Rite®
Bergamid™ A70 G30 U NC284	PolyOne Corporation	Nylon 66	Bergamid™
Braskem PP C7082-30NA	Braskem Europe GmbH	PP Impact Copolymer	Braskem PP